During processing, plastics are frequently exposed to high stresses. These include, above all, shear and temperature within the scope of the residence time of the manufacturing process in order to achieve a homogeneous plastic melt for further processing. The stress of the manufacturing process can lead to molecular degradation, which can have a negative effect on the product properties. Since it makes sense to take molecular degradation into account for many processes, a test stand for material characterization was designed and a regression equation was derived for the mathematical description of the degradation behavior. With the help of this regression equation, a prediction of the expected material degradation can be made, provided that the shear rate, the temperature and the associated residence time are known.

In the context of plastics recycling, plastics are processed several times. With each new melting and extrusion the plastic is damaged, which can have a negative effect on product properties. To counteract material damage, special additives such as chain extenders can be used, which are intended to lead to post-polymerization during processing. A linear chain extension is important here, as branching and crosslinking can lead to uncontrolled changes in the plastic’s properties. To investigate the suitability of specialized linear chain extenders for polyamides, a polyamide-6 was processed several times and the molar mass distribution was evaluated after each extrusion cycle. Three series of tests were carried out. First, the plastic was regranulated five times without additives and twice with different concentrations of chain extenders on a twin-screw extruder. The results of the study show that not only can molar mass degradation be prevented with the appropriate additive, it is even possible to achieve a material buildup during processing. In our experiments, the polydispersity of the molar mass distribution remained nearly identical despite multiple extrusions. Thus, reactive extrusion makes it possible for the corresponding plastics to be processed several times without the molar mass decreasing. If a sufficiently pure material flow can be ensured during recycling, the number of possible reprocessings of the plastic can be significantly increased without the need to add virgin material.

During the processing of thermoplastics, polymers are subjected to high stress. As a result of this stress, the polymer chains break, leading to a lower molar mass. This further leads to a lower viscosity of the plastic melt and, eventually, to poorer mechanical properties of the manufactured plastic product. Especially in the context of recycling plastics, this poses a challenge to process technology and product properties. This work aims is to provide a prediction of the material degradation under known stress, so that, for example, a process design that is gentle on the material can be carried out. In order to be able to predict material degradation under a load, a test stand for defined material degradation was designed. The test stand allows for material damaging under a defined temperature, shear rate and residence time. At the same time, the test stand can be used to measure the viscosity, which is used to describe the degradation behavior, since the viscosity correlates with the molar mass. The measured decrease in viscosity under stress can be used to predict material damage under the influencing variables of temperature, shear rate and residence time by means of a test plan and a suitable mathematical description of the measured data. The mathematical description can thus be integrated into simulation environments for plastics processing, so that a simulation of the material degradation can be carried out, if necessary also taking the viscosity reduction into account.

In the processing of plastic granules to the finished product, the plastic melt is exposed to high shear rates and high temperatures for a specific residence ti