Although pre-treatment parameters for subtractive computer-aided design/computer-aided manufacturing (CAD/CAM) materials have been thoroughly investigated, data regarding additive restorative materials designed for permanent use in the oral cavity are scarce. This study investigated the effects of abrasive materials and blasting pressure on the bond strength of 3D-printed resins used in permanent restorations. A total of n = 44 test specimens additively manufactured from Formlabs' `Permanent Crown Resin' were prepared. Three groups with n = 11 specimens were airborne-particle abraded with 50 µm aluminium oxide at 1 bar, 2 bar or 3 bar. The control group did not receive any further airborne-particle abrasion after post-processing with 50 µm glass beads. Cylindrical superstructures were bonded to the prepared surfaces using RelyX Unicem 2. The bonded specimens were then subjected to artificial ageing via thermocycling. Subsequently, shear bond strength (sbs) tests were conducted. Data were analysed with the Kruskal-Wallis test (α = 0.05). After post-processing with glass beads, average shear bond strength values of 10.13 ± 7.62 MPa were achieved. When using aluminium oxide and 1 bar blasting pressure, significantly higher average sbs values of 25.57 ± 7.04 MPa were revealed (p = 0.009). The bond strength increased with higher blasting pressures (28.14 ± 6.35 MPa at 2 bar (p = 0.005); 30.15 ± 6.46 MPa at 3 bar (p < 0.001)). However, the shear tests revealed increased failure within the specimen base at higher blasting pressures. Bond strength significantly improved when airborne-particle abrasion with aluminium oxide was applied. However, increased airborne-particle abrasion pressure led to more failures at the base plate level of the specimens. Aluminium oxide increases the adhesive strength of 3D-printed dental restorative materials. Although the adhesive bond increased slightly with increasing airborne-particle abrasion pressure, the 3D restorative materials also exhibited an increased failure rate within the restorative material in the shear bond strength test with increasing blasting pressure.

Objective: To investigate the effectiveness of individual oral health care training (IndOHCT) on dental plaque removal and denture cleaning in hospitalized geriatric inpatients. Background: The literature reveals neglect of hygiene and oral care in people aged over 65 years, especially in persons in need of care. Hospitalized geriatric inpatients have poorer dental health than those non-hospitalized. Furthermore, the existing literature reporting on oral healthcare training interventions for hospitalized geriatric inpatients is scarce. Materials and Methods: This pre-post-controlled intervention study dichotomized 90 hospitalized geriatric inpatients into an intervention group (IG) and a control group (CG). Inpatients in the IG received IndOHCT. Oral hygiene was assessed using the Turesky modified Quigley–Hein index (TmQHI) and the denture hygiene index (DHI), at baseline (T0), at a second examination (T1a), and after supervised autonomous tooth brushing and denture cleaning (T1b). The influence of the Mini Mental State Examination (MMSE), Geriatric Depression Scale (GDS), and Barthel Index (BI) scores on oral hygiene was examined. Results: There was no significant plaque reduction on teeth or dentures between T0 and T1a in either group. Between T1a and T1b, plaque reduction on the teeth was more effective in the IG than in the CG (p < 0.001). Inpatients with 1–9 remaining teeth removed significantly more dental plaque than inpatients with 10 or more remaining teeth. Inpatients with lower MMSE scores (p = 0.021) and higher age (p = 0.044) reached higher plaque reduction on dentures. Conclusions: IndOHCT improved oral and denture hygiene in geriatric inpatients by enabling them to clean their teeth and dentures more effectively.

Purpose: To measure surface roughness before and after wear‐tests of two different prefabricated composite veneers and compare them to ceramic veneers and human dental enamel.Materials and Methods: Roughness (Ra‐values) of two prefabricated composite veneers (Visalys Veneer Chairside (VIS) and Componeer (COM)) were compared to lithium disilicate Veneers (e.max CAD) and dental enamel (DENT) in vitro. In total n = 45 specimens per material and enamel samples were used for wear‐tests. Wear‐out tests were conducted by abrasion tests with a toothbrush simulator (22,000 strokes/ 100 g load; approximately equal to two years of cleansing) and erosion tests were carried out using citric acid (pH 1.57). Ra‐ and Sa‐values were detected by white light interferometer before and after wear‐tests. Data were analyzed with ANOVA followed by Games‐Howell post hoc test and t‐test (α = 0.05).Results: At baseline the lowest Ra‐ and Sa‐values were found in VIS (Ra: 0.01 µm; Sa: 0.04 µm) while DENT revealed significantly higher surface roughness (Ra: 0.11 µm, p < 0.05; Sa: 0.30, p = 0.186). COM had significantly higher Ra‐values (Ra: 0.10 µm; Sa: 0.22 µm) after abrasion, while e.max CAD was most resistant to the treatments (Ra: 0.01 µm, p < 0.05; Sa: 0.05 µm, p < 0.05). Compared to DENT all veneers were significantly less affected by citric acid (p < 0.001).Conclusions: Prefabricated composite veneers have demonstrated less wear after abrasion and erosion tests compared to DENT, nevertheless, they revealed more wear compared to e.max CAD.

The purpose of this study was to investigate the functional load capacity of the periodontal ligament (PDL) in a full arch maxilla and mandible model using a numerical simulation. The goal was to determine the functional load pattern in multi- and single-rooted teeth with full and reduced periodontal support. CBCT data were used to create 3D models of a maxilla and mandible. The DICOM dataset was used to create a CAD model. For a precise description of the surfaces of each structure (enamel, dentin, cementum, pulp, PDL, gingiva, bone), each tooth was segmented separately, and the biomechanical characteristics were considered. Finite Element Analysis (FEA) software computed the biomechanical behavior of the stepwise increased force of 700 N in the cranial and 350 N in the ventral direction of the muscle approach of the masseter muscle. The periodontal attachment (cementum–PDL–bone contact) was subsequently reduced in 1 mm increments, and the simulation was repeated. Quantitative (pressure, tension, and deformation) and qualitative (color-coded images) data were recorded and descriptively analyzed. The teeth with the highest load capacities were the upper and lower molars (0.4–0.6 MPa), followed by the premolars (0.4–0.5 MPa) and canines (0.3–0.4 MPa) when vertically loaded. Qualitative data showed that the areas with the highest stress in the PDL were single-rooted teeth in the cervical and apical area and molars in the cervical and apical area in addition to the furcation roof. In both single- and multi-rooted teeth, the gradual reduction in bone levels caused an increase in the load on the remaining PDL. Cervical and apical areas, as well as the furcation roof, are the zones with the highest functional stress. The greater the bone loss, the higher the mechanical load on the residual periodontal supporting structures.