The use of cement emulsified asphalt mortar (CA mortar) in the track structure of high-speed speed railways has been gaining considerations by many researchers due to its coupled merits of the strength of cement as well as the flexibility of asphalt material. The asphalt to cement ratio (A/C) and the compatibility among constituent materials are crucial to the properties of CA mortar. To improve the performance properties and application of CA mortar, it is imperative to have a broad understanding of the composition mechanisms and compatibility between constituent materials. This paper summarizes interesting research outcomes related to the composition and properties of CA mortar. The consumption of water by cement promotes the breakdown of emulsified asphalt, likewise, the adsorption of asphalt droplets on the surface of cement grains retards the hydration process of cement. An appropriate A/C is required for the cement hydration rate to match the speed of demulsification of asphalt emulsion. Depending on the type and properties for which the CA mortar is designed to possess, the A/C ranges from 0.2 to 0.6 for type 1 (CAM I), and 0.6 to 1.2 for type 2 (CAM II). This paper also discusses measures taken to improve performance properties, compatibility, the interaction between constituent materials of CA mortar, and the use of additives as a partial replacement of cement in CA mortar production. The current review also suggests areas of interest for future research studies. This paper is useful to those who aim to understand or study the composition mechanisms and performance properties of CA mortar.

Brittle fracture is a typical mechanical characteristic of high-strength self-compacting concrete, and the research on its toughening modification remains the highlight in the engineering field. To understand the effect of toughening materials (including polymer latex powders, rubber particles, and polyethylene fibers) on the mechanical behavior of C80 high-strength self-compacting concrete under static loading, the failure mode, mechanical strength, strain field, and crack opening displacement (COD) of prepared high-strength self-compacting concrete under compressive, splitting, and flexural loads were studied based on digital image technology (DIC). The corresponding mechanism is also discussed. The results show that the hybrid of polymer latex powders, rubber particles, and polyethylene fibers can increase the crack path and inhibit the development of macrocracks in concrete, thus turning the fracture behavior of concrete from brittle to ductile. The addition of toughening materials reduced the compressive and flexural strengths of high-strength self-compacting concrete, but it increased the splitting strength. DIC showed that the incorporation of toughening materials promoted the redistribution of strain and reduced the degree of strain concentration in high-strength self-compacting concrete. The evolution of COD in high-strength self-compacting concrete can be divided into two stages, including the linear growth stage and the plastic yield stage. The linear growth stage can be extended by incorporating toughening materials. The COD and energy absorption capacity of concrete were enhanced with the addition of toughening materials, and the best enhancement was observed with the hybrid of polymer latex powders, rubber particles, and polyethylene fibers. Overall, this research provides a reference for exploring effective technical measures to improve the toughness of high-strength self-compacting concrete.

Multilayer films can achieve advanced properties and a wide range of applications. The heterogeneous interface plays an important role in the performances of multilayer films. In this paper, the effects of the interface of Ba(Mg_1/3Ta_2/3)O₃/PbZr_0.52Ti_0.48O₃ (BMT/PZT) thin films on dielectric behavior and temperature stability are investigated. The heterogeneous interface structures are characterized by Auger electron spectroscopy (AES). The PZT-BMT interface is different from the BMT-PZT interface in thickness. For the PZT-BMT interface, the PZT thin films are diffused to the whole BMT layers, and the interface thickness is about 90 nm, while the BMT-PZT interface’s thickness is only about 8.6 nm. The presence of heterogeneous interfaces can improve the performances of BMT/PZT thin films and expand their applications. The dielectric constant of BBPP thin films is significantly lower than BPBP thin films, while the dielectric loss is exactly the opposite. The more interfaces there are, the greater the dielectric constant. The relationship between the electric-field-dependent dielectric constant curve and the P-E curve is established. The equivalent interface barrier of the diode is used to show that the dielectric peaks under the positive and negative voltage are different. Similarly, heterogeneous interfaces show a certain improvement in dielectric tunability and temperature stability.