This review provides a report on the properties and recent advances in the application of chitosan and chitosan-based materials in cosmetics. Chitosan is a polysaccharide that can be obtained from chitin via the deacetylation process. Chitin most commonly is extracted from cell walls in fungi and the exoskeletons of arthropods, such as crustaceans and insects. Chitosan has attracted significant academic interest, as well as the attention of the cosmetic industry, due to its interesting properties, which include being a natural humectant and moisturizer for the skin and a rheology modifier. This review paper covers the structure of chitosan, the sources of chitosan used in the cosmetic industry, and the role played by this polysaccharide in cosmetics. Future aspects regarding applications of chitosan-based materials in cosmetics are also mentioned.

The process of crosslinking improves the physicochemical properties of biopolymer-based composites, making them valuable for biomedical applications. EDC/NHS-crosslinked collagen materials have a significant potential for tissue engineering applications, due to their enhanced properties and biocompatibility. Chemical crosslinking of samples can be carried out in several ways, which is crucial and has a direct effect on the final properties of the obtained material. In this study, the effect of crosslinking conditions on the properties of collagen films using EDC and NHS was investigated. Studies included FTIR spectroscopy, AFM, swelling and degradation tests, mechanical testing and contact angle measurements. Evaluation of prepared collagen films indicated that both crosslinking agents and crosslinking conditions influenced film properties. Notable alternations were observed in the infrared spectrum of the sample, to which EDC was added directly to the fish collagen solution. The same sample indicated the lowest Young modulus, tensile strength and breaking force parameters and the highest elongation at break. All samples reached the maximum swelling degree two hours after immersion in PBS solution; however, the immersion-crosslinked samples exhibited a significantly lower degree of swelling and were highly durable. The highest roughness was observed for the collagen film crosslinked with EDC, whereas the lowest was observed for the specimen crosslinked with EDC with NHS addition. The crosslinking agents increased the surface roughness of the collagen film, except for the sample modified with the addition of EDC and NHS mixture. All films were characterized by hydrophilic character. The films’ modification resulted in a decrease in their hydrophilicity and wettability. Our research allows for a comparison of proposed EDC/NHS crosslinking conditions and their influence on the physicochemical properties of fish collagen thin films. EDC and NHS are promising crosslinking agents for the modification of fish collagen used in biomedical applications.

The aim of this research was the modification of fish collagen films with various amounts of dialdehyde starch (DAS). Film properties were examined before and after the cross-linking process by DAS. Prepared biopolymer materials were characterized by Fourier Transform Infrared Spectroscopy and Atomic Force Microscopy. Moreover, the mechanical, thermal and swelling properties of the films were evaluated and the contact angle was measured. Research has shown that dialdehyde starch applied as a cross-linking agent influences collagen film properties. Mechanical testing indicated a decrease in Young’s Modulus and an increase in breaking force, elongation at break, and tensile strength parameters. Results for contact angle were significantly higher for collagen films cross-linked with DAS; thus, the hydrophilicity of samples decreased. Modified samples presented a lower swelling degree in PBS than native collagen films. However, the highest values for the degree of swelling among the modified specimens were obtained from the 1% DAS samples, which were 717% and 702% for 1% and 2% collagen, respectively. Based on AFM images and roughness values, it was noticed that DAS influenced collagen film surface morphology. The lowest value of Rq was observed for 2%Coll_2%DAS and was approximately 10 nm. Analyzing thermograms for collagen samples, it was observed that pure collagen samples were less thermally stable than cross-linked ones. Dialdehyde starch is a promising cross-linking agent for collagen extracted from fish skin and may increase its applicability.

In this work, blend films were prepared by blending 2% chitosan (CS) and 0.5% konjac glucomannan (KGM) solutions. Five ratios of the blend mixture were implemented (95:5, 80:20, 50:50, 20:80, and 5:95), and a pure CS film and a pure KGM film were also obtained. All the polymeric films were evaluated using FTIR spectroscopy, mechanical testing, SEM and AFM imaging, thermogravimetric analyses, swelling and degradation analyses, and contact angle measurements. The CS/KGM blends were assessed for their miscibility. Additionally, the blend films’ properties were evaluated after six months of storage. The proposed blends had good miscibility in a full range of composition proportions. The blend samples, compared to the pure CS film, indicated better structural integrity. The surface structure of the blend films was rather uniform and smooth. The sample CS/KGM 20:80 had the highest roughness value (Rq = 12.60 nm). The KGM addition increased the thermal stability of films. The blend sample CS/KGM 5:95 exhibited the greatest swelling ability, reaching a swelling degree of 946% in the first fifteen minutes of the analysis. Furthermore, the addition of KGM to CS improved the wettability of the film samples. As a result of their good mechanical properties, surface characteristics, and miscibility, the proposed CS/KGM blends are promising materials for topical biomedical and cosmetic applications.

Chitosan is increasingly utilized in combination with melatonin in novel formulations for a wide range of therapeutic applications. As a biocompatible and biodegradable polymer, chitosan exhibits notable properties, including antioxidant, antimicrobial, moisturizing, and absorption capabilities, in addition to a high potential for chemical modification due to its functional groups. These characteristics make it a valuable material in biomedical, pharmaceutical, cosmetic, food packaging, and environmental applications. Melatonin, an indoleamine primarily synthesized in the pineal gland but also found in various peripheral organs and in diverse organisms—including plants, bacteria, and fungi—has been extensively investigated for its antioxidant, anti-apoptotic, and anti-inflammatory activities, as well as its roles in immunomodulation, mitochondrial function, and melanin biosynthesis. This review summarizes recent advances in the combined use of chitosan and melatonin, with emphasis on their synergistic effects in wound healing, anti-cancer therapies, tissue engineering (i.e., skin and bone regeneration), and drug delivery systems. Additional potential applications are discussed in the context of cosmetology, aesthetic medicine, and veterinary practice.

Biopolymers represent a significant class of materials with potential applications in skin care due to their beneficial properties. Resveratrol is a natural substance that exhibits a range of biological activities, including the scavenging of free radicals and anti-inflammatory and anti-aging effects. In this study, chitosan/konjac glucomannan resveratrol-enriched thin films were prepared. The enrichment of biomaterials with active ingredients is a common practice, as it allows the desired properties to be obtained in the final product. To characterize the films, several analyses were performed, including infrared spectroscopy, imaging of the samples by SEM and AFM techniques, swelling analysis in pH 5.5 and 7.4, mechanical and antioxidant assays, contact angle measurements, and determination of the resveratrol release profile under the skin mimicking conditions. Resveratrol incorporation into the matrices resulted in modifications to the chemical structure and film morphology. The mechanical characteristics of films with additives were found to undergo deterioration. The sample containing 10% of resveratrol exhibited a higher swelling degree than other films. The resveratrol-modified films demonstrated a notable antioxidant capacity, a reduced contact angle, and enhanced wettability. The resveratrol release occurred rapidly initially, with a maximum of 84% and 56% of the substance released depending on the sample type. Thus, the proposed formulations have promising properties, in particular good swelling capacity, high antioxidant potential, and improved wettability, and may serve as skin dressings after further investigation.