The aim of this work is to study the effect of high-temperature compaction (HTC) upon the polymorphism and the mechanical behavior of an additively manufactured (AM) carbon fiber-reinforced polyamide (PA6). Different pressure and temperature levels during HTC were tested to determine the overall effect on the mechanical behavior and material crystalline composition. Treated, carbon fiber-reinforced PA6 samples were analyzed using differential scanning calorimetry, X-ray diffraction, thermogravimetric analysis, scanning electron microscopy, and three-point bending testing. When considered with respect to as-printed samples, an HTC temperature of 190 °C combined with 80 psi pressure resulted in an increased flexural modulus and strength of 47% and 58%, respectively. This increase was attributed to the decrease in AM-induced cracking, voids (both inside and between the beads), and crystalline solid-state transition in the PA6. The effect of pressure and temperature on the crystalline structure was discussed in terms of an increased degree of crystallinity and the amount of α-phase. Therefore, HTC can help overcome some limitations of traditional annealing, which can result in recrystallization-induced cracking which can lead to material embrittlement. The proposed HTC method demonstrates the potential in improving the mechanical behavior of AM thermoplastic composites.

To maximize the capabilities of nano- and micro-class satellites, which are limited by their size, weight, and power, advancements in deployable mechanisms with a high deployable surface area to packaging volume ratio are necessary. Without progress in understanding the mechanics of high-strain materials and structures, the development of compact deployable mechanisms for this class of satellites would be difficult. This paper presents fabrication, experimental testing, and progressive failure modeling to study the deformation of an ultra-thin composite beam. The research study examines the deformation modes of a post-deployed boom under repetitive pure bending loads using a four-point bending setup and bending collapse failure under eccentric buckling. The material and fabrication challenges for ultra-thin, high-stiffness (UTHS) composite boom are discussed in detail. The continuum damage mechanics (CDM) model for the beam is calibrated using experimental coupon testing and was used for a finite element explicit analysis of the boom. It is shown that UTHS can sustain a bending radius of 14 mm without significant fiber and matrix damage. The finite element model accurately predicts the localized transverse fiber damage under eccentric buckling and buckling stiffness of 15.6 N/mm. The results of the bending simulation were found to closely match the experimental results, indicating that the simulation accurately shows deformation stages and predicts damage to the material. The findings of this research provide a better understanding of the structure characteristics with the progressive damage model of the UTHS boom, which can be used for designing a complex deployable payload for nano-micro-class satellites.

An experimental investigation of interlaminar toughness for post-cured through-thickness reinforcement (PTTR) skin–stringer sub-element is presented. The improvement in the crack resistance capability of skin–stringer samples was shown through experimental testing and finite element analysis (FEA) modeling. The performance of PTTR was evaluated on a pristine and initial-disbond of the skin–stringer specimen. A macro-scale pin–spring modeling approach was employed in FEA using a non-linear spring to capture the pin failure under the mixed-mode load. The experimental results showed a 15.5% and 20.9% increase in strength for the pristine-PTTR and initial-disbond PTTR specimens, respectively. The modeling approach accurately represents the overall structural response of PTTR laminate, including stiffness, adhesive strength, crack extension scenarios and progressive pin failure modes. This modeling approach can be beneficial for designing damage-tolerant structures by exploring various PTTR arrangements for achieving improved structural responses.

For large-scale engineering problems, it has been generally accepted that domain-partitioning algorithms are highly desirable for general-purpose finite element analysis (FEA). This paper presents a heuristic numerical algorithm that can efficiently partition any transportation network (or any finite element mesh) into a specified number of subdomains (usually depending on the number of parallel processors available on a computer), which will result in “minimising the total number of system BOUNDARY nodes” (as a primary criterion) and achieve “balancing work loads” amongst the subdomains (as a secondary criterion). The proposed seven-step heuristic algorithm (with enhancement features) is based on engineering common sense and observation. This current work has the following novelty features: (i) complicated graph theories that are NOT needed and (ii) unified treatments of transportation networks (using line elements) and finite element (FE) meshes (using triangular, tetrahedral, and brick elements) that can be performed through transforming the original network (or FE mesh) into a pseudo-transportation network which only uses line elements. Several examples, including real-life transportation networks and finite element meshes (using triangular/brick/tetrahedral elements) are used (under MATLAB computer environments) to explain, validate and compare the proposed algorithm’s performance with the popular METIS software.