Photocatalysis performs excellently when degrading organic pollutants, but the photocatalytic degradation rate is not high for most photocatalysts due to their narrow sunlight adsorption range and high recombination rate of electron hole pairs. Herein, we use V₂C-MXene with a wide sunlight adsorption range to couple ZnO porous nanosheets and form ZnO/MXene hybrids using a facile electrostatic self-assembly method. The ZnO/MXene hybrids acquired demonstrated improved photochemical efficiency in breaking down methylene blue (MB) when contrasted with porous ZnO nanosheets. The degradation rate of MB reached 99.8% under UV irradiation for 120 min after the ZnO/MXene hybrid formation, while 38.6% was attained by the ZnO porous nanosheets. Moreover, photodegradation rate constants (k) were calculated as 3.05 × 10⁻³ and 5.42 × 10⁻² min⁻¹ for ZnO porous nanosheets and ZnO/MXene hybrids, respectively, indicating that the photodegradation performance was enhanced by 17.8 times after the modification of V₂C. This was probably because the modification of V₂C can increase the specific surface area to provide more sites for MB adsorption, widen the sunlight adsorption range to produce good photothermal effect, and facilitate the transfer of photogenerated carriers in ZnO to promote the reaction of more photogenerated carriers with MB. Hence, this work offers a simple approach to creating effective photocatalysts for breaking down organic contaminants.

Highly-transparent trivalent erbium ion doped calcium fluoride (5 mol % Er:CaF2) ceramics were fabricated by a hotpressing (HP) method using high-purity Er:CaF2 nanoparticles, which were synthesized by co-precipitation method. The mean grain size of the nanoparticles was about 24.7 nm. The nanoparticles were sintered at 600 °C, 700 °C, 800 °C and 900 °C, respectively, for 30 min under a uniaxial pressure of 30 MPa and vacuum of 10−3 Pa with 1 mol % lithium fluoride (LiF) as sintering additive. The 5 mol % Er:CaF2 ceramics sintered at 800 °C exhibits high density and pore-free microstructure with an average grain size of about 8 μm. The optical transmittance of the transparent ceramics is close to 85 % at visible and nearinfrared wavelengths. The strong and broad absorptions peaks corresponding to characteristic absorption of trivalent erbium ions make the ceramics a potential candidate for infrared and upconversion laser operating.