In this work, bio-based hydrogel composites of xanthan gum and cellulose fibers were developed to be used both as soil conditioners and topsoil covers, to promote plant growth and forest protection. The rheological, morphological, and water absorption properties of produced hydrogels were comprehensively investigated, together with the analysis of the effect of hydrogel addition to the soil. Specifically, the moisture absorption capability of these hydrogels was above 1000%, even after multiple dewatering/rehydration cycles. Moreover, the soil treated with 1.8 wt% of these materials increased the water absorption capacity by approximately 60% and reduced the water evaporation rate, due to the formation of a physical network between the soil, xanthan gum and cellulose fibers. Practical experiments on the growth of herbaceous and tomato plants were also performed, showing that the addition of less than 2 wt% of hydrogels into the soil resulted in higher growth rate values than untreated soil. Furthermore, it has been demonstrated that the use of the produced topsoil covers helped promote plant growth. The exceptional water-regulating properties of the investigated materials could allow for the development of a simple, inexpensive and scalable technology to be extensively applied in forestry and/or agricultural applications, to improve plant resilience and face the challenges related to climate change.

This study was focused on the development of novel bio-based and biodegradable hydrogels constituted of xanthan gum (XG) reinforced with wood fibers, to be used as eco-sustainable topsoil covers (TSCs) in support of reforestation and agricultural efforts in arid conditions. At this aim, hydrogels were developed by cross-linking XG with citric acid (CA), sodium trimetaphosphate (STMP) or tannic acid (TA) at different concentrations. Samples cross-linked with CA and TA exhibited the highest dimensional stability and exceptional water absorption capability, even after multiple absorption/drying cycles. Hydrogels with 50, 60, and 100 phr of CA displayed water vapor permeance values of about 9.5·10⁻⁶ g/(Pa·s·m²), i.e., comparable to commercial woven PP mulching films. The average penetration resistance of the produced hydrogels was twice that of the commercial one. The presence of wood fibers in the hydrogels provided dimensional stability and minimal shrinkage after exposure to outdoor conditions for two months (15.4 % for sample with 60 phr of CA). Furthermore, after 7 months of exposure, more than 60 % of the sample mass was biodegraded. This research demonstrated the potential of xanthan gum/wood fibers based hydrogels as TSCs with superior water-regulating properties, thus offering a simple, cost-effective and scalable technology for forestry and agriculture applications.

The aim of this study was to investigate the effect of different types of natural cellulose-based fillers on the properties of Xanthan gum (XG) in order to develop novel bio-based soil conditioners (SCs) that could be used in forestry and agricultural applications. Rheological measurements highlighted that SCs with cellulose fillers characterized by a high aspect ratio and low oxide ash content exhibited an average increase of 21% in yield stress compared to neat Xanthan gum. The presence of cellulose fillers in the composites resulted in a slower water release than that of neat XG, limiting the volumetric shrinkage during the drying process. Furthermore, an analysis of the water absorption and water retention capacity of soils treated with the different SCs was carried out, demonstrating that the addition of 1.8 wt.% of SC with optimized composition to the soil led to an increase in water absorption capacity from 34% up to 69%. From the soil water retention curves, it was observed that the addition of SCs significantly increased the amount of water effectively available for plants in the area between field capacity and permanent wilting point (100–1000 kPa). From practical experiments on grass growth, it was observed that these SCs improved the water regulation of the soil, thus increasing the probability of plant survival under drought conditions.

The impact of climate change has become increasingly severe in forests, where droughts and strong winds on the one hand and extreme rainfall events on the other hand can damage forest ecosystems. To mitigate the effects of drought and enhance soil water retention capacity, three types of soil conditioners (SCs), labeled SC_R, SC_CG, and SC_ZZC, were developed as part of the European project ONEforest. All the conditioners are based on Xanthan gum and have different types and amounts of fillers with diverse cellulose fiber lengths. These can offer the potential to optimize the SC characteristics, e.g., water absorption, water retention, and mechanical stability. This paper focuses on the influence of fillers in the SCs on the geotechnical properties of forest soils from Ljubelj in the Alpine part of Slovenia (S1), Catalonia, northeastern Spain (S2), and Heldburg, Germany (S3). The results show an increase of 53% to 100% in the water absorption of treated soil. A less favorable impact of the SCs was found on the drained shear strength and the compressibility. The drained shear strength of untreated forest soils in a saturated state was S1 c′ = 4.4 kPa, φ′ = 33.5°; S2 c′ = 1.4 kPa, φ′ = 30.0°; and S3 c′ = 12 kPa, φ′ = 28.0°. The addition of SCs results in a reduction in the drained shear strength of saturated mixtures. The reduction depends on the dosage of added SC—whether it is a low (L) or a high (H) dosage. For instance, when the soil S1 was treated with a low dosage of the soil conditioner SC_R, it demonstrated a cohesion (c′) of 11 kPa and a friction angle (φ′) of 27.0°. However, increasing the dosage of the SC_R led to a decrease in both the cohesion and the friction angle for the same soil (c′ = 7.7 kPa, φ′ = 25.0°). Additionally, the type of soil conditioner also impacts the drained shear strength. Among the mixtures with a high dosage of the SC_R, SC_CG, or SC_ZZC, those containing the SC_CG with the longest fibers stand out, demonstrating the highest friction angle. Therefore, longer fibers can be a promising component of the SCs to reduce the negative influence of XG on the mechanical properties of treated soils.