The purpose of this study is to evaluate the changes in physical properties and biocompatibilities caused by thermocycling of CAD/CAM restorative materials (lithium disilicate, zirconia reinforced lithium silicate, polymer-infiltrated ceramic network, resin nanoceramic, highly translucent zirconia). A total of 225 specimens were prepared (12.0 × 10.0 × 1.5 mm) and divided into three groups subjected to water storage at 37 °C for 24 h (control group), 10,000 cycles in distilled water at 5–55 °C (first aged group), and 22,000 cycles in distilled water at 5–55 °C (second aged group) [(n= 15, each]). The nanoindentation hardness and Young’s modulus (nanoindenter), surface roughness (atomic force microscopy (AFM)), surface texture (scanning electron microscopy (FE-SEM)), elemental concentration (energy dispersive spectroscopy (EDS)) and contact angle were evaluated. The morphology, proliferation and adhesion of cultured human gingival fibroblasts (HGFs) were analyzed. The data were analyzed using one-way ANOVA and Tukey’s test (p < 0.05). The results showed that the nanoindentation hardness and Young’s modulus were decreased after thermocycling aging. Cell viability and proliferation of the material decreased with aging except for the highly translucent zirconia. Zirconia-reinforced lithium silicate exhibited significantly lower cell viability compared to other materials. The surface roughnesses of all groups increased with aging. Cell viability and Cell adhesion were influenced by various factors, including the surface chemical composition, hydrophilicity, surface roughness, and topography.

Han SY, et al. J Adv Prosthodont. 2020 Oct;12(5):251-258. https://doi.org/10.4047/jap.2020.12.5.251

This study assessed the changes in the mechanical and surface properties of the transition zone in multilayered translucent monolithic zirconia subjected to long-term hydrothermal aging. A total of 360 disk-shaped specimens (diameter: 15.0 mm; thickness: 1.2 mm) were prepared using conventional (3Y-TZP in LT; ZL, 4Y-TZP in MT; ZM) and multilayered translucent zirconia (5Y-TZP in MT Multi; ZT, 3Y/5Y-TZP in Prime; ZP) among IPS e.max ZirCAD blocks. Specimens were divided into three groups (n = 30) and aged in the autoclave at 134 °C under 0.2 MPa for 0 h (control group), 5 h (first aged group), and 10 h (second aged group). The mechanical and surface properties of the transition zone in the multilayered translucent zirconia were investigated, followed by statistical analysis (α = 0.05). Before and after aging, ZL (1102.64 ± 41.37 MPa) and ZP (1014.71 ± 139.86 MPa) showed the highest biaxial flexural strength (BFS); ZL showed the highest Weibull modulus (31.46) and characteristic strength (1121.63 MPa); and ZT exhibited the highest nanoindentation hardness (20.40 ± 1.80 GPa) and Young’s modulus (284.90 ± 20.07 GPa). After aging, ZL (116.75 ± 9.80 nm) exhibited the highest surface roughness (Ra); the monoclinic phase contents in ZL and ZP increased; and surface uplifts, microcracks, and irregular defects caused by phase transformation appeared on ZL and ZP surfaces. The 3Y/5Y-TZP transition zone exhibited flexural strength, Vickers hardness, phase distribution changes, and surface microstructure changes similar to those of 3Y-TZP before and after aging; however, the surface roughness was lower than that of 3Y-TZP and higher than those of 4Y-TZP and 5Y-TZP after aging. The mechanical and surface characteristics, excluding BFS and Vickers hardness, were influenced by the yttrium oxide content in each zone and the aging process.