The homogeneous distribution of carbon nanotubes (CNTs) in the Cu matrix and good interfacial bonding are the key factors to obtain excellent properties of carbon nanotube-reinforced Cu-based composites (CNT/Cu). In this work, silver-modified carbon nanotubes (Ag-CNTs) were prepared by a simple, efficient and reducer-free method (ultrasonic chemical synthesis), and Ag-CNTs-reinforced copper matrix composites (Ag-CNTs/Cu) were fabricated by powder metallurgy. The dispersion and interfacial bonding of CNTs were effectively improved by Ag modification. Compared to CNTs/Cu counterparts, the properties of Ag-CNTs/Cu samples were significantly improved, with the electrical conductivity of 94.9% IACS (International Annealed Copper Standard), thermal conductivity of 416 W/m·k and tensile strength (315 MPa). The strengthening mechanisms are also discussed.

In this study, an innovative internal oxidation-powder metallurgy combined process was employed to controllably generate nano-sized Cr₂O₃ reinforcing phases within the Cu matrix. The Cu/Cr₂O₃ composites were successfully fabricated using the hot-press sintering (HP) method, and a systematic comparison was made between the microstructure and mechanical properties of composites prepared by internal oxidation and external addition methods. The results show that internal oxidation primarily occurs during the sintering process rather than ball milling. Compared with external addition, the internal oxidation method effectively prevents particle aggregation and achieves a uniform distribution of Cr₂O₃ particles in the Cu matrix. When the Cr content reaches 5 wt%, the Cu-5%Cr composite exhibits optimal mechanical properties, with a yield strength of 282.7 MPa and ultimate tensile strength of 355 MPa, representing increases of 43% and 34% over pure copper, respectively, while maintaining an elongation of 12.6%. The Cr₂O₃ particles generated via internal oxidation enhance their strength through Orowan strengthening and dislocation pinning, thereby significantly improving mechanical performance without compromising plasticity. This research provides a novel process optimization approach for developing high-performance dispersion-strengthened copper matrix composites.

With the acceleration of industrialization and the increase in car ownership, exhaust pollution has become a major global environmental challenge. Harmful gases such as carbon monoxide (CO) and nitrogen oxides (NO_x) are discharged into the air, forming acid rain, producing chemical smog, and destroying the ozone layer. This causes severe harm to the environment and human health. Rh-based catalysts play a crucial role in exhaust gas treatment due to their excellent performance in selective catalytic reduction (SCR) and direct nitrogen oxide decomposition (DND) of NO_x. However, deactivation limits their stability and service life, increasing costs and restricting industrial application. This paper reviews the reaction mechanisms of Rh-based catalysts in SCR and DND reactions, discusses deactivation mechanisms, and proposes improvement strategies. It provides theoretical basis and practical guidance for the development of efficient and stable catalysts for exhaust gas treatment.