Mechanical properties of plasma-irradiated and surface-coated wood plastic composites (WPCs) have been investigated in this paper. WPCs were developed by injection molding technique using wood fiber (WF) as reinforcement and polypropylene (PP) as matrix. The short, discontinuous WF was compounded with thermoplastic PP at varying weight fractions of 0 wt%, 25 wt% (WP25), and 50 wt% (WP50) to yield tensile test specimens in accordance with JIS K7139-A32 standards. Subsequently, plasma treatment was performed on the test-pieces, followed by surface coating by immersion in acrylic resin liquid containing homogeneously dispersed TEMPO-oxidized cellulose nanofibers (CNF). The results indicate an increase in surface roughness after plasma irradiation, but surface coating of the specimens with acrylic paint and CNF decreased their surface roughness by ∼50% in comparison to the untreated specimens. Plasma treatment and surface coating also increased the tensile strength of neat PP, WP25 and WP50 specimens by 5.4–7.1%, 3.5–3.7% and 3.0–3.6%, respectively, whereas their fracture strains tended to decrease. Compared to the untreated specimens, the surface-coated specimens generally displayed higher tensile strength. This finding is a corroboration that the observed increase in strength is highly contingent on the adhesion between the specimen surface and the coating layer than on the improvement in surface roughness. Thus, it is inferable that surface coating could be of great importance in enhancing the mechanical performance of WPCs.

The depletion of conventional materials and their adverse environmental impacts have prompted a shift toward sustainable alternatives in composite materials engineering. In pursuit of this objective, this study investigated the mechanical properties of polypropylene matrix composites reinforced with Cordenka, an artificial cellulose fiber, and compared them to those reinforced with ramie, a natural cellulose fiber. Continuous strand composites were developed using the Multi-Pin-assisted Resin Infiltration (M-PaRI) process. The strands were subsequently sectioned into 15 mm lengths and injection-molded into dumbbell and strip specimens for mechanical characterization. The results showed that 20 wt% Cordenka/PP composites exhibited a tensile strength of 68.7 MPa, 2.04 times higher than neat PP and 1.66 times greater than the 20 wt% ramie/PP composites. Impact testing further demonstrated that Cordenka/PP composites absorbed 2 to 2.5 times more impact energy than ramie/PP composites, regardless of the presence of notches. Fiber length analysis indicated that Cordenka fibers maintained their length beyond the critical fiber length, allowing for efficient stress transfer and acting as a more effective reinforcement compared to ramie fibers, which were below this threshold. Consequently, the Cordenka/PP composites exhibited significantly enhanced mechanical performance. Scanning electron microscopy (SEM) analysis revealed fewer fiber pullouts in ramie-reinforced composites, suggesting superior interfacial adhesion to the PP matrix, although it did not translate to higher mechanical properties. These findings underscore the potential of Cordenka as a sustainable alternative to synthetic, non-biodegradable fibers in PP composites, providing improved mechanical properties and promising prospects for advanced composite applications.

Ibsen Henric Ongidi, Fadhila Yusuf Abdulsalaam, Thomas Mombo Amuti, Wycliffe O. Kaisha, Kirsteen O. Awori, Anne Naipanoi Pulei. Anat Cell Biol 2021;54:241-8. https://doi.org/10.5115/acb.20.230

This study investigates the effect of polymer film lamination on the tensile performance of wood fiber-reinforced polypropylene (WP) composites. Neat polypropylene (PP) and WP containing 25 wt% wood fiber were injection-molded and laminated with 0.1 mm PP or polyethylene terephthalate (PET) films using a compatible adhesive. Four configurations were examined: unlaminated (0S), single-sided half-length (1S-H), single-sided full-length (1S-F), and double-sided full-length (2S-F). Mechanical properties and fracture morphology were characterized by uniaxial tensile tests and scanning electron microscopy (SEM), alongside measurements of surface roughness. PET lamination produced the greatest strength enhancements, with 2S-F specimens achieving gains of 12% for PP and 21% for WP, whereas PP lamination gave minimal or negative effects, except for a 5% increase in WP. Strength improvements were attributed to surface smoothing and suppression of crack initiation, as confirmed by roughness measurements and SEM observations. PET’s higher stiffness and strength accounted for its superior reinforcement relative to PP. Fractographic analysis revealed flat regions near specimen corners—interpreted as crack initiation sites—indicating that lamination delayed crack propagation. The results demonstrate that PET film lamination is an effective and practical post-processing strategy for enhancing the mechanical performance of wood–plastic composites.