The deformation shrinkage of a poly(lactide-co-glycolide) (PLGA) fibrous material seriously affects its biomedical application. To demonstrate the underlying shrinking mechanism and to find a method to prevent the shrinkage of an electrospun PLGA membrane, we investigated the shrinking behavior of PLGA electrospun membranes under various test conditions and discussed the underlying shrinking mechanism. The results indicated that the shrinkage of the electrospun PLGA membrane was mainly regulated by the glass transition of its polymer fiber; the temperature and liquid environment were found to be the two main factors leading to the shrinkage of the electrospun PLGA membrane through affecting its glass transition. Then a heat stretching (HS) technique was proposed by us to stabilize the electrospun PLGA membrane. After HS treatment, the glass transition temperature (T_g) of the electrospun PLGA membrane could increase from 48.38 °C to 54.55 °C. Our results indicated that the HS-treated membranes could maintain a high area percentage of 90.89 ± 2.27% and 84.78 ± 3.36% after immersion respectively in PBS and blood at 37 °C for 2 hours. Further experiments confirmed that the HS technique could also stabilize the dimensional structure of the electrospun PDLLA membrane in PBS and blood at 37 °C. This study provides an effective strategy for preventing the shrinkage of electrospun polyester biomaterials in a physiological environment that may benefit both the material structural stability and the in vivo biological performance.

Processibility and biodegradability of conductive polymers are major concerns when they are applied to tissue regeneration. This study synthesizes dissolvable and conductive aniline trimer-based polyurethane copolymers (DCPU) and processes them into scaffolds by using electrospinning with different patterns (random, oriented, and latticed). The effects of topographic cue changes on electrical signal transmission and further regulation of cell behaviors concerning bone tissue are researched. Results show that DCPU fibrous scaffolds possessed good hydrophilicity, swelling capacity, elasticity, and fast biodegradability in enzymatic liquid. In addition, the conductivity and efficiency of electrical signal transmission can be tuned by changing the surface’s topological structure. Among them, oriented DCPU scaffolds (DCPU-O) showed the best conductivity with the lowest ionic resistance value. Furthermore, the viability and proliferation results of bone mesenchymal stem cells (BMSCs) demonstrate a significant increase on three DCPU scaffolds compared to AT-free scaffolds (DPU-R). Especially, DCPU-O scaffolds exhibit superior abilities to promote cell proliferation because of their unique surface topography and excellent electroactivity. Concurrently, the DCPU-O scaffolds can synergistically promote osteogenic differentiation in terms of osteogenic differentiation and gene expression levels when combined with electrical stimulation. Together, these results suggest a promising use of DCPU-O fibrous scaffolds in the application of tissue regeneration.