Aging is indispensable for balancing the strength and ductility of selective laser melted (SLM) precipitation hardening steels. This work investigated the influence of aging temperature and time on the microstructure and mechanical properties of SLM 17-4 PH steel. The 17-4 PH steel was fabricated by SLM under a protective argon atmosphere (99.99 vol.%), then the microstructure and phase composition after different aging treatments were characterized via different advanced material characterization techniques, and the mechanical properties were systematically compared. Coarse martensite laths were observed in the aged samples compared with the as-built ones, regardless of the aging time and temperature. Increasing the aging temperature resulted in a larger grain size of the martensite lath and precipitation. The aging treatment induced the formation of the austenite phase with a face-centered cubic (FCC) structure. With prolonged aging treatment, the volume fraction of the austenite phase increased, which agreed with the EBSD phase mappings. The ultimate tensile strength (UTS) and yield strength gradually increased with increasing aging times at 482 °C. The UTS reached its peak value after aging for 3 h at 482 °C, which was similar to the trend of microhardness (i.e., UTS = 1353.4 MPa). However, the ductility of the SLM 17-4 PH steel decreased rapidly after aging treatment. This work reveals the influence of heat treatment on SLM 17-4 steel and proposes an optimal heat-treatment regime for the SLM high-performance steels.

Hydrogen is an ideal feedstock fuel for solid oxide fuel cells (SOFCs). The steam reforming of methane (SRM) is the predominant method of producing hydrogen. However, the process of SRM relies on the involvement of a catalyst, and the reforming efficiency is constrained by the limited surface area in the traditional catalyst system. In this study, a mixer structure is applied to improve the mixing of the methane. Nano-sized pores are introduced to the struts of the mixer structure, forming a hierarchical structure, to effectively reduce the weight and increase the surface area of the self-catalytic reactors, hence increasing the catalytic efficiency. The hierarchical structure increases the reforming efficiency at all temperatures, and the level of improvement reaches its peak when the conversion rate of methane increases by 192% at 800 °C and by 40% at 900 °C compared to the self-catalyst without a hierarchical structure.