Several studies have shown that the dentin-resin interface is unstable due to poor infiltration of resin monomers into the demineralized dentin matrix. This phenomenon is related to the incomplete infiltration of the adhesive system into the network of exposed collagen fibrils, mainly due to the difficulty of displacement and subsequent replacement of trapped water between interfibrillar spaces, avoiding adequate hybridization within the network of collagen fibrils. Thus, unprotected fibrils are exposed to undergo denaturation and are susceptible to cyclic fatigue rupture after being subjected to repetitive loads during function. The aqueous inclusions within the hybrid layer serve as a functional medium for the hydrolysis of the resin matrix, giving rise to the activity of esterases and collagenolytic enzymes, such as matrix metalloproteinases, which play a fundamental role in the degradation process of the hybrid layer. Achieving better interdiffusion of the adhesive system in the network of collagen fibrils and the substrate stability in the hybrid layer through different strategies are key events for the interfacial microstructure to adequately function. Hence, it is important to review the factors related to the mechanisms of degradation and stabilization of the hybrid layer to support the implementation of new materials and techniques in the future. The enzymatic degradation of collagen matrix, together with resin leaching, has led to seeking strategies that inhibit the endogenous proteases, cross-linking the denudated collagen fibrils and improving the adhesive penetration removing water from the interface. Some of dentin treatments have yielded promising results and require more research to be validated. A longer durability of adhesive restorations could resolve a variety of clinical problems, such as microleakage, recurrent caries, postoperative sensitivity, and restoration integrity.

The physicochemical features of the avian eggshell membrane play an essential role in the process of calcium carbonate deposition during shell mineralization, giving rise to a porous mineralized tissue with remarkable mechanical properties and biological functions. The membrane could be useful by itself or as a bi-dimensional scaffold to build future bone-regenerative materials. This review focuses on the biological, physical, and mechanical properties of the eggshell membrane that could be useful for that purpose. Due to its low cost and wide availability as a waste byproduct of the egg processing industry, repurposing the eggshell membrane for bone bio-material manufacturing fulfills the principles of a circular economy. In addition, eggshell membrane particles have has the potential to be used as bio-ink for 3D printing of tailored implantable scaffolds. Herein, a literature review was conducted to ascertain the degree to which the properties of the eggshell membrane satisfy the requirements for the development of bone scaffolds. In principle, it is biocompatible and non-cytotoxic, and induces proliferation and differentiation of different cell types. Moreover, when implanted in animal models, it elicits a mild inflammatory response and displays characteristics of stability and biodegradability. Furthermore, the eggshell membrane possesses a mechanical viscoelastic behavior comparable to other collagen-based systems. Overall, the biological, physical, and mechanical features of the eggshell membrane, which can be further tuned and improved, make this natural polymer suitable as a basic component for developing new bone graft materials.

Hybrid biomimetic materials aim to replicate the organic-inorganic constructs of mineralized tissues. During eggshell formation, the outer surface of the eggshell membrane (ESM) promotes calcium carbonate nucleation, while the inner one prevents mineralization toward the egg white and yolk. In the current study, the outer surface of the ESM acted as a heteronucleant in calcium phosphate precipitation by the vapor diffusion sitting drop method, while the inner one remained unmineralized. The aim was to fabricate a 2D biomaterial with dual functions, osteoinductive on one side and protective against cell invasion on the other side. The microstructural, physicochemical, morphological, and mechanical properties of the mineralized ESM were characterized by XRD, TGA, XPS, FTIR/Raman, HR-SEM, and mechanical testing techniques. The cytocompatibility and osteoinductive ability were assessed by biological assays of cell viability, proliferation, and osteogenic differentiation on human mesenchymal stromal cells (hMSCs). Results indicate that the outer surface of the ESM induces the heterogeneous precipitation of carbonate-apatite phase depicting biomimetic features. In addition, the apatite/ESM shows a much higher cytocompatibility than the pristine ESM and promotes the osteogenic differentiation of hMSCs more efficiently. Overall, the apatite/ESM composite exhibits compositional, crystalline, mechanical, and biological properties that resemble those of mineralized tissues, rendering it an approachable and novel material especially useful in guided tissue/bone regeneration.

Objective. The aim of this systematic review was to provide an overview of available scientific evidence regarding the comparative efficacy of computer-aided design (CAD) and computer-aided manufacturing (CAM) glass fiber posts with prefabricated and metal cast posts for the restoration of endodontically treated teeth (ETT). Methods. This systematic review was conducted following the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) guidelines. Electronic and manual searches were performed using the PubMed, SciELO, Cochrane, ScienceDirect, Web of Science, and EBSCO databases. The reference lists of the selected papers were reviewed to identify relevant papers. There were no year restrictions, and eligible studies were those in English publications and describing in vitro studies evaluating intraradicular retainers (IRs) for (i) fracture resistance, (ii) bond strength, (iii) adaptation, and (iv) cement layer thickness. Literature reviews, systematic reviews, meta-analyses, case reports, in vitro studies with <8 specimens, and noncomparative trials involving prefabricated or metal cast posts were excluded. The authors of this review independently screened the search results, extracted data, and assessed the risk of bias. Results. No significant differences were found in fracture resistance between prefabricated and CAD/CAM glass fiber posts or between CAD/CAM glass fiber and metal cast posts, although the latter demonstrated higher fracture resistance than the prefabricated glass fiber posts. Restoration with a full crown was not necessary to increase the fracture resistance in the presence of the ferrule effect. CAD/CAM glass fiber and metal cast posts had higher bond strength, lower nanoleakage, and better adaptation to the root canal. Conclusions. Despite the heterogeneity of methodologies and results reported, the results of these studies indicated that the CAD/CAM glass fiber and metal cast posts showed greater efficacy in terms of fracture resistance, retention, and adaptation, compared to prefabricated glass fiber posts.