In this study, porous scaffold materials based on polyvinyl alcohol (PVA) and gelatin (Gel) were successfully fabricated and characterized. The mechanism of the reaction, morphology, and crystallinity were investigated by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). In addition, thermogravimetric analysis (TGA) was performed together with differential scanning calorimetry (DSC) for examining the thermostability and phase transformation of the scaffolds. Degradation and swelling studies of PVA/Gel composite scaffold materials were performed in phosphate-buffered saline. Finally, the mechanical performances had been determined. According to the results, the polymer matrix that was formed by the combination of PVA and gelatin had better thermal stability. The synthesized composite scaffold was amorphous in nature. The addition of gelatin did not affect the fishbone-like microstructure of PVA, which ensures the excellent mechanical properties of the PVA scaffold. The denaturation temperature and elastic modulus of the PVA scaffold were improved by the gelatin addition, but the physical and chemical properties of the PVA scaffold were weakened when the gelatin content exceeded 10%. In addition, the PVA-10G sample has suitable degradability. Therefore, the PVA/Gel composite scaffold might potentially be applied in the field of tissue engineering that demands high strength.

Hydrogel adhesives are attractive for applications in intelligent soft materials and tissue engineering, but conventional hydrogels usually have poor adhesion. In this study, we designed a strategy to synthesize a novel adhesive with a thin hydrogel adhesive layer integrated on a tough substrate hydrogel. The adhesive layer with positive charges of ammonium groups on the polymer backbones strongly bonds to a wide range of nonporous materials’ surfaces. The substrate layer with a dual hydrogen bond system consists of (i) weak hydrogen bonds between N,N-dimethyl acrylamide (DMAA) and acrylic acid (AAc) units and (ii) strong multiple hydrogen bonds between 2-ureido-4[1H]-pyrimidinone (UPy) units. The dual hydrogen-bond network endowed the hydrogel adhesives with unique mechanical properties, e.g., toughness, highly stretchability, and insensitivity to notches. The hydrogel adhesion to four types of materials like glass, 316L stainless steel, aluminum, Al₂O₃ ceramic, and two biological tissues including pig skin and pig kidney was investigated. The hydrogel bonds strongly to dry solid surfaces and wet tissue, which is promising for biomedical applications.

Collagen (Col) hydrogels are an important biomaterial with many applications in the biomedical sector. However, deficiencies, including insufficient mechanical properties and a rapid rate of biodegradation, hamper their application. In this work, nanocomposite hydrogels were prepared by combining a cellulose nanocrystal (CNC) with Col without any chemical modification. The high-pressure, homogenized CNC matrix acts as nuclei in the collagen’s self-aggregation process. The obtained CNC/Col hydrogels were characterized in terms of their morphology, mechanical and thermal properties and structure by SEM, rotational rheometer, DSC and FTIR, respectively. Ultraviolet-visible spectroscopy was used to characterize the self-assembling phase behavior of the CNC/Col hydrogels. The results showed an accelerated assembling rate with the increasing loading of CNC. The triple-helix structure of the collagen was preserved with a dosage of CNC of up to 15 wt%. The CNC/Col hydrogels demonstrated an improvement in both the storage modulus and thermal stability which is attributed to the interaction between the CNC and collagen by the hydrogen bonds.

Cellulose nanofibers (CNFs) are highly promising nanocarrier materials, boasting excellent drug adsorption and loading potential due to their tunable hydrophilic/lipophilic interfaces. This study is the first to report the successful synthesis of maleic anhydride-modified CNFs (MA-CNFs) via the esterification of CNFs using a solvent-free molten maleic anhydride (MA) system, and it systematically evaluates MACNFs’ dual adsorption performance for water-soluble and lipophilic drugs. A new characteristic peak at 1723 cm⁻¹ in FT-IR confirms the formation of ester bonds, proving the successful grafting of MA onto CNFs. XRD analysis shows that the crystallinity slightly increases from 72.56% to 74.06%, indicating the reaction mainly occurs in the amorphous region. After modification, the material’s hydrophobicity is significantly enhanced (water contact angle: ~63.3° for CNFs vs. ~74.9° for MA-CNFs), and its BET specific surface area rises sharply from 5.03 to 26.29 m²/g. These structural advantages collectively enable MA-CNFs to have adsorption capacities for folic acid (FA, water-soluble) and vitamin E acetate (VEA, lipophilic) that are 1.15 and 2.04 times those of CNFs, respectively. The results demonstrate MA-CNFs are high-performance functional materials fabricated via a green method, with good biocompatibility.