In this study, the mechanical and microstructural properties of Al-Zn-Mg-Cu-Zr cast alloy with 0.1% Sc under homogeneous, dissolution, and T6 and thermomechanical treatments with the aim of increasing the volume fraction of MgZn₂. Al₃(Sc,Zr) reinforcing precipitates were examined by hardness, microscopic examinations, tensile tests and software analysis. The results showed that, firstly, the hardness results are well proportional to the results of the tensile properties of alloys and, secondly, the strength of the alloy with thermomechanical treatments compared to T6 treatments increased from 492 MPa to 620 MPa and the elongation increased from 8% to 17% and was 100% upgraded. Microstructural and fracture cross section investigations showed that Al₃(Sc,Zr) nanosize dispersoids were evenly distributed among MgZn₂ dispersoids and the alloy fracture was of semi-ductile type and nanosize dispersoids less than 10 nm were observed at the end of the dimples in the fracture section. The volume fraction of nanosize dispersoids in the whole microstructure of thermomechanical treatment samples was also much higher than that of T6 heat treated samples, so that the percentage of Al₃(Sc,Zr) precipitates arrived from less than 1% in T6 operation to 8.28% in the quench-controlled thermomechanical operation (with 50% deformation). The quality index (QI) in thermomechanical treatment samples is 19% higher than T6 samples, so that this index has increased from 641 in T6 operation to 760 in samples under thermomechanical treatment due to precipitate morphology, volume fraction of precipitates, their uniform distribution in the matrix, and nano sized precipitates in samples under thermomechanical treatment.

Titanium and its alloys are known as one of the most significant metallic materials used in the orthopedic and dental implants due to their excellent mechanical properties, corrosion resistance, and biocompatibility. One of the main issues in dental implant is the fabrication of the biomaterials that have early and sufficiently strong bonding with the surrounding bone. In the present study, porous Ti6Al4V scaffolds were synthesized using the powder metallurgy with various amounts of magnesium. The specimens were sintered at 950 ℃, close to magnesium vaporization point, because of the remaining magnesium in the scaffolds. The microstructure and mechanical properties of the specimens were investigated. Electrochemical characterization was carried out to indicate the effect of porosity on corrosion resistance. This investigation showed that the porous Ti6Al4V scaffolds containing 5–10 volume percent of magnesium with 28–31% porosity as a semi-degradable implant could be an advanced alternative for clinical application under load-bearing conditions such as dental implants which require two factors of strength and osteointegration.

The current research investigates the effect of ultrafine microstructure resulted from Quench and Partitioning (Q&P) process on obtaining ultra-high strengths in a low-alloy steel with 4wt.% carbon. The purpose of Q&P heat treatment is to enrich the austenite with carbon by partitioning of carbon from supersaturated martensite to austenite, in order to stabilize it to the room temperature. The microstructure, consequently, is consists of martensite, retained austenite and in some conditions bainite. Two-step Q&P heat treatment with quench and partitioning temperatures equal to 120°C and 300°C respectively were applied to the samples at different times. Mechanical behavior was studied by tensile test. The microstructure of the samples was observed using SEM, and TEM and to quantify the amount of retained austenite X-ray diffraction was used. The retained austenite grain size was estimated to be about 0.5 µm and the highest amount of retained austenite obtained was 10 vol%. All samples showed a yield strength and a tensile strength of above 900MPa and 1500MP respectively. The yield strength increased with increase in partitioning time, whereas tensile strength showed an inverse behavior. The elongation in samples varied from 5% to 9% which seemed to not have a direct connection with the amount of retained austenite, but instead it was related to the ferritic structures formed during partitioning such as coalesced martensite, bainite and tempered martensite.