A layered double hydroxide (LDH) surface was employed as a substrate for growing silver nanoparticles (NPs). An efficient method to produce stable silver/silver chloride nanoparticles supported on the ZnAl-LDH surface was developed. NPs of AgCl were grown on the ZnAl-LDH surface by using AgNO₃ as the silver source. The ZnAl-LDH in chloride form acts as a nucleating agent, and depending on the pH of the LDH dispersion, AgClNPs with different dimensions were obtained. In particular AgClNPs with a diameter of 60 nm were formed at pH 5. The AgClNPs supported on LDH sheets were partially reduced by different reducing agents (NaBH₄ and formaldehyde) resulting in a Ag/AgCl-LDH nanocomposite. The silver chloride and silver NP dimensions were evaluated by X-ray powder diffraction, field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). UV-Vis spectra of the samples upon reduction showed a band centred at 415 nm due to the surface plasmon resonance of silver nanoparticles with a diameter of about 10 nm, in agreement with the TEM analysis. The AgCl-LDH and Ag/AgCl-LDH nanocomposites, subjected to antimicrobial tests, exhibited good antimicrobial activity against both Gram-negative (Pseudomonas aeruginosa) and Gram-positive (Staphylococcus epidermidis and S. aureus) bacteria and yeast (Candida albicans). The nanocomposites were also studied for their ability to release silver by obtaining release curves, under conditions of antibacterial assays. Finally, the nanocomposites antibacterial behavior, as a function of time, was investigated by performing time–kill experiments using S. aureus and Candida albicans.

The selectivity towards halides and the mechanism of ion exchange of ZnAl-LDH in the chloride form (X⁻ = F⁻, Br⁻, I⁻) were investigated using ion exchange isotherms of Cl⁻/X⁻.

PdNPs stabilized on exfoliated layered zirconium phosphate–carboxyphosphonate nanosheets as an efficient catalytic system for the Suzuki coupling.

Resveratrol, because of its low solubility in water and its high membrane permeability, is collocated in the second class of the biopharmaceutical classification system, with limited bioavailability due to its dissolution rate. Solid dispersion of resveratrol supported on Magnesium DiHydroxide (Resv@MDH) was evaluated to improve solubility and increase bioavailability of resveratrol. Fluorimetric microscopy analysis displays three types of microparticles with similar size: Type 1 that emitted preferably fluorescence at 445 nm with bandwidth of 50 nm, type 2 that emitted preferably fluorescence at 605 nm with bandwidth of 70 nm and type 3 that is non-fluorescent. Micronized pure resveratrol displays only microparticles type 1 whereas type 3 are associated to pure magnesium dihydroxide. Dissolution test in simulated gastric environment resveratrol derived from Resv@MDH in comparison to resveratrol alone displayed better solubility. A 3-fold increase of resveratrol bioavailability was observed after oral administration of 50 mg/kg of resveratrol from Resv@MDH in rabbits. We hypothesize that type 2 microparticles represent magnesium dihydroxide microparticles with a resveratrol shell and that they are responsible for the improved resveratrol solubility and bioavailability of Resv@MDH.

Control of the interlayer composition and morphology of LDH by proper choice of salt, nitrate or chloride and the amount of urea.