Intercalation-based inorganic materials that change their colours upon ion insertion/extraction lay an important foundation for existing electrochromic technology. However, using only such inorganic electrochromic materials, it is very difficult to achieve the utmost goal of full-colour tunability for future electrochromic technology mainly due to the absence of structural flexibility. Herein, we demonstrate an ultracompact asymmetric Fabry-Perot (F-P) nanocavity-type electrochromic device formed by using partially reflective metal tungsten as the current collector and reflector layer simultaneously; this approach enables fairly close matching of the reflections at both interfaces of the WO₃ thin layer in device form, inducing a strong interference. Such an interference-enhanced device that is optically manipulated at the nanoscale displays various structural colours before coloration and, further, can change to other colours including blue, red, and yellow by changing the optical indexes (n, k) of the tungsten oxide layer through ion insertion.

Electrochromic materials were discovered in the 1960s when scientists observed reversible changes between the light and dark states in WO₃ thin films under different voltages. Since then, researchers have identified various electrochromic material systems, including transition metal oxides, polymer materials, and small molecules. However, the electrochromic phenomenon has rarely been observed in non-metallic elemental substances. Herein, we propose the development of non-metallic iodine electrodeposition-based electrochromic dynamic windows using a water-in-salt electrolyte containing iodine ions. The unique electrolyte environment and solvation structure of the water-in-salt electrolyte suppress the dissolution and shuttle effect of iodine, thereby achieving a different reaction pathway compared to traditional electrolytes. This pathway involves a reversible solid-liquid transition between solid iodine and solvated iodide ions. The iodine electrodeposition-based electrochromic dynamic window demonstrates a high optical contrast of 76.0% with near colour neutrality and excellent cycling stability. A practical 400 cm² complementary dynamic window is fabricated to demonstrate good electrochromic performance, including high optical contrast, a near colour-neutral opaque state, fast response time, uniform modulation, and polarity-switchable functionality.