Herein, the synthesis and characterization of a novel composite biopolymer scaffold—based on equine type I collagen and hyaluronic acid—were described by using a reaction in heterogeneous phase. The resulting biomimetic structure was characterized in terms of chemical, physical, and cytotoxicity properties using human-derived lymphocytes and chondrocytes. Firstly, FT-IR data proved a successful reticulation of hyaluronic acid within collagen structure with the appearance of a new peak at a wavenumber of 1735 cm⁻¹ associated with ester carbonyl stretch. TGA and DSC characterizations confirmed different thermal stability of cross-linked scaffolds while morphological analysis by scanning electron microscopy (SEM) suggested the presence of a highly porous structure with open and interconnected void areas suitable for hosting cells. The enzymatic degradation profile confirmed scaffold higher endurance with collagenase as compared with collagen alone. However, it was particularly interesting that the mechanical behavior of the composite scaffold showed an excellent shape memory, especially when it was hydrated, with an improved Young’s modulus of 9.96 ± 0.53 kPa (p ≤ 0.001) as well as a maximum load at 97.36 ± 3.58 kPa compared to the simple collagen scaffold that had a modulus of 1.57 ± 0.08 kPa and a maximum load of 36.91 ± 0.24 kPa. Finally, in vitro cytotoxicity confirmed good product safety with human lymphocytes (viability of 81.92 ± 1.9 and 76.37 ± 1.2 after 24 and 48 h, respectively), whereas excellent gene expression profiles of chondrocytes with a significant upregulation of SOX9 and ACAN after 10 days of culture indicated our scaffold’s ability of preserving chondrogenic phenotype. The described material could be considered a potential tool to be implanted in patients with cartilage defects.

In orthopedics, titanium (Ti)-alloy implants, are often considered as the first-choice candidates for bone tissue engineering. An appropriate implant coating enhances bone matrix ingrowth and biocompatibility, improving osseointegration. Collagen I (COLL) and chitosan (CS) are largely employed in several different medical applications, for their antibacterial and osteogenic properties. This is the first in vitro study that provides a preliminary comparison between two combinations of COLL/CS coverings for Ti-alloy implants, in terms of cell adhesion, viability, and bone matrix production for probable future use as a bone implant. Through an innovative spraying technique, COLL–CS–COLL and CS–COLL–CS coverings were applied over Ti-alloy (Ti-POR) cylinders. After cytotoxicity evaluations, human bone marrow mesenchymal stem cells (hBMSCs) were seeded onto specimens for 28 days. Cell viability, gene expression, histology, and scanning electron microscopy evaluations were performed. No cytotoxic effects were observed. All cylinders were biocompatible, thus permitting hBMSCs’ proliferation. Furthermore, an initial bone matrix deposition was observed, especially in the presence of the two coatings. Neither of the coatings used interferes with the osteogenic differentiation process of hBMSCs, or with an initial deposition of new bone matrix. This study sets the stage for future, more complex, ex vivo or in vivo studies.