The effects of the addition of different nanosilica dosages (0.5%, 1%, and 1.5% with respect to cement) on compressive strength and durability properties of concrete with water/binder ratios 0.65, 0.55, and 0.5 were investigated. Water sorptivity, apparent chloride diffusion coefficient, electrical resistivity, and carbonation coefficient of concrete were measured. The results showed that compressive strength significantly improved in case of water/binder = 0.65, while for water/binder = 0.5 no change was found. Increasing nanosilica content, the water sorptivity decreased only for water/binder = 0.55. The addition of 0.5% nanosilica decreased the apparent chloride diffusion coefficient for water/binder = 0.65 and 0.55; however, higher nanosilica dosages did not decrease it with respect to reference value. The resistivity was elevated by 0.5% nanosilica for all water/binder ratios and by 1.5% nanosilica only for water/binder = 0.5. The carbonation coefficient was not notably affected by increasing nanosilica dosages and even adverse effect was observed for water/binder = 0.65. Further information of microstructure was also provided through characterization techniques such as X-ray diffraction, thermal gravimetric analysis, mercury intrusion porosimetry, and scanning electron microscopy. The effectiveness of a certain nanosilica dosage addition into lower strength mixes was more noticeable, while, for the higher strength mix, the effectiveness was less.

Carbon nanotubes (CNTs) have shown promise for improving the mechanical performance of cement composites through crack-bridging and frictional pull-out. The interactive behaviors between CNTs and cement matrix act are crucial in optimizing the reinforcement of CNTs in cement composites. This study investigates the effects of nano-silica (NS) sol-gel on the interactive behaviors of CNTs and the cement matrix through a series of experiments and analyses. UV-visible spectrometer results show that CNTs are well-dispersed in suspension and the addition of NS has a negligible effect on the stability of CNT dispersion. Calorimetry tests and dynamic mechanical analysis demonstrate the nucleation and frictional performance of CNTs in cement matrix, respectively. The paper shows that the physical adsorption of NS on the CNT surface could result in the acceleration of cement hydration. Morphology observation confirms that a denser interface between CNTs and cement hydrates is formed. Finally, the improved interaction between CNTs and cement hydrates leads to a substantial increase in friction between CNTs and the cement matrix under periodic loading. NS may act as an ideal admixture for improving both the interactive behaviors between CNTs and cement matrix and the damping properties of cement composite.

Effects of nanosilica on cement hydration have been broadly investigated in the literature and early age cement hydration, as a whole, has been mainly considered, disregarding the substages of the hydration. The hydration of cement is characterized by different substages and nanosilica effect on the hydration could be a result of diverse, even contradictory, behavior of nanosilica in individual stages of the hydration. In this study, effects of nanosilica on different substages of cement hydration are investigated. Isothermal calorimetry results show that at early ages (initial 72 hours) the effects of nanosilica depend on the phenomenon by which the hydration is governed: when the hydration is chemically controlled, that is, during initial reaction, dormant period, and acceleratory period, the hydration rate is accelerated by adding nanosilica; when the hydration is governed by diffusion process, that is, during postacceleratory period, the hydration rate is decelerated by adding nanosilica. The Thermal Gravimetric Analysis on the samples at the hardened state (after 28 days of curing) reveals that, after adding nanosilica, the hydration degree slightly increased compared to the plain paste.