Chitin-glucan complex (CGC) hydrogels were fabricated through a freeze–thaw procedure for biopolymer dissolution in NaOH 5 mol/L, followed by a dialysis step to promote gelation. Compared to a previously reported methodology that included four freeze–thaw cycles, reducing the number of cycles to one had no significant impact on the hydrogels’ formation, as well as reducing the total freezing time from 48 to 18 h. The optimized CGC hydrogels exhibited a high and nearly spontaneous swelling ratio (2528 ± 68%) and a water retention capacity of 55 ± 3%, after 2 h incubation in water, at 37 °C. Upon loading with caffeine as a model drug, an enhancement of the mechanical and rheological properties of the hydrogels was achieved. In particular, the compressive modulus was improved from 23.0 ± 0.89 to 120.0 ± 61.64 kPa and the storage modulus increased from 149.9 ± 9.8 to 315.0 ± 76.7 kPa. Although the release profile of caffeine was similar in PBS and NaCl 0.9% solutions, the release rate was influenced by the solutions’ pH and ionic strength, being faster in the NaCl solution. These results highlight the potential of CGC based hydrogels as promising structures to be used as drug delivery devices in biomedical applications.

The main goal of this study was to screen different lignocellulosic materials for their ability to support the cell growth of the yeast Komagataella pastoris and the production of xylitol. Several lignocellulosic materials, namely banana peels, brewer’s spent grains (BSGs), corncobs, grape pomace, grape stalks, and sawdust, were subjected to dilute acid hydrolysis to obtain sugar rich solutions that were tested as feedstocks for the cultivation of K. pastoris. Although the culture was able to grow in all the tested hydrolysates, a higher biomass concentration was obtained for banana peels (15.18 ± 0.33 g/L) and grape stalks (14.58 ± 0.19 g/L), while the highest xylitol production (1.51 ± 0.07 g/L) was reached for the BSG hydrolysate with a xylitol yield of 0.66 ± 0.39 g/g. Cell growth and xylitol production from BSG were improved by detoxifying the hydrolysate using activated charcoal, resulting in a fourfold increase of the biomass production, while xylitol production was improved to 3.97 ± 0.10 g/L. Moreover, concomitant with arabinose consumption, arabitol synthesis was noticed, reaching a maximum concentration of 0.82 ± 0.05 g/L with a yield on arabinose of 0.60 ± 0.11 g/g. These results demonstrate the feasibility of using lignocellulosic waste, especially BSG, as feedstock for the cultivation of K. pastoris and the coproduction of xylitol and arabitol. Additionally, it demonstrates the use of K. pastoris as a suitable microorganism to integrate a zero-waste biorefinery, transforming lignocellulosic waste into two high-value specialty chemicals with high market demand.