Meltless recycling technique has been utilized to overcome the lack of primary resources, focusing on reducing the usage of energy and materials. Hot press was proposed as a novel direct recycling technique which results in astoundingly low energy usage in contrast with conventional recycling. The aim of this study is to prove the technical feasibility of this approach by characterizing the recycled samples. For this purpose, AA6061 aluminium chips were recycled by utilizing hot press process under various operating temperature (T_s = 430, 480, and 530 °C) and holding times (t_s = 60, 90, and 120 min). The maximum mechanical properties of recycled chip are Ultimate tensile strength (UTS) = 266.78 MPa, Elongation to failure (ETF) = 16.129%, while, for surface integrity of the chips, the calculated microhardness is 81.744 HV, exhibited at T_s = 530 °C and t_s = 120 min. It is comparable to theoretical AA6061 T4-temper where maximum UTS and microhardness is increased up to 9.27% and 20.48%, respectively. As the desired mechanical properties of forgings can only be obtained by means of a final heat treatment, T5-temper, aging after forging process was employed. Heat treated recycled billet AA6061 (T5-temper) are considered comparable with as-received AA6061 T6, where the value of microhardness (98.649 HV) at 175 °C and 120 min of aging condition was revealed to be greater than 3.18%. Although it is quite early to put a base mainly on the observations in experimental settings, the potential for significant improvement offered by the direct recycling methods for production aluminium scrap can be clearly demonstrated. This overtures perspectives for industrial development of solid state recycling processes as environmentally benign alternatives of current melting based practices.

In this study, the response surface methodology (RSM) and desirability function (DF) were utilized to optimize the recycling conditions of aluminum (AA6061) chips, in the presence of particulate alumina (Al₂O₃), to obtain a metal matrix composite of recycled aluminum (MMC-Al_R) using hot press forging processes. The effects of temperature (430–530 °C) and holding time (60–120 min) were investigated. The introduction of 2.0 wt. % of Al₂O₃ to the aluminum matrix was based on preliminary research and some pilot tests. This study employed the 2^k factorial design of experiments that should satisfy the operating temperatures (T) of 430 °C and 530 °C with holding times (t) of 60 min and 120 min. The central composite design (CCD) was utilized for RSM with the axial and center point to evaluate the responses to the ultimate tensile strength (UTS), elongation to failure (ETF), and microhardness (MH). Based on RSM, with the desirability of 97.6%, the significant parameters T = 530 °C and t = 120 min were suggested to yield an optimized composite performance with UTS = 317.99 MPa, ETF = 20.45%, and MH = 86.656 HV. Three confirmation runs were performed based on the suggested optimum parameters, and the error revealed was less than 25%. The mathematical models suggested by RSM could adequately describe the MMC-Al_R responses of the factors being investigated.

Ecological manageability in manufacturing these days is a dire and exceptional issue and the principle concerns are identified with increasingly proficient utilization of energy and materials. Recycling can save a large amount greenhouse gas emissions, particularly in the case of aluminum. The parameter on the innovative technique on the direct recycling was investigated by employing design of experiments, via hot press forging process (DR-HPF). Thus, reutilizing of aluminum chips AA6061 with full factorial 3² design of experiment comprising a variety of working temperature and holding time were employed. Central composite design (CCD) was applied to outline the experiments towards evaluating the influences of the hot press forging parameters to the three responses; ultimate tensile strength (UTS), elongation to failure (ETF), and global warming potential (GWP). In conjunction with this, the environmental impacts associated with DR-HPF process are evaluated alongside the resultant conventional recycling (CR) by using re-melting route as indication. Experimental measurements, literature analysis and industrial data were merged to acquire the analysis of aluminum recycling life cycle. Clear conclusions were successfully drawn through the attained results on the outlook proposed by solid state direct recycling for the purpose of reducing the environmental effects by taking material and energy conservation as one of the most essential impacting factor. The global warming potential of a DR-HPF route gives a significant environmental impact where it is reduced up to 69.2% in comparison to the conventional (melting) routes.

A method of solid-state recycling aluminum alloy using hot press forging process was studied as well as the possibility of the recycled chip to be used as secondary resources. This paper presents the results of recycled AA6061 aluminium alloy chip using different operating temperature for hot press forging process. Mechanical properties and microstructure of the recycled specimens and as-received (reference) specimen were investigated. The recycled specimens exhibit a good potential in the strength properties. The result for yield strength (YS) and ultimate tensile strength (UTS) at the minimum temperature 430°C is 25.8 MPa and 27.13 MPa. For the maximum operating temperature 520°C YS and UTS are 107.0MPa and 117.53 MPa. Analysis for different operating temperatures shows that the higher temperatures giving better result on mechanical properties and finer microstructure. The strength of recycled specimen increases due to the grain refinement strengthening whereas particle dispersion strengthening has minor effects. In this study, the recycled AA6061 chip shows the good potential in strengthening as the comparison of using only 17.5% of suggested pressure (70.0/400.0) MPa, the UTS exhibit 35.8% (117.58/327.69) MPa. This shows a remarkable potential of direct recycling by using hot press forging process.

Compared to the recycling process by remelting, hot extrusion significantly reduces the energy consumption and CO₂ emission and ensures good mechanical and microstructural properties. This study investigates the effects of reinforcing aluminium AA6061 chips with mixed boron carbide (B₄C) and zirconia (ZrO₂) particles by employing a design of experiment (DOE) under 550 °C processing temperature and three hours preheating time. The findings showed that compressive strength (CS) and hardness increased with up to 5% added particles, and beyond 5%, the yielded values decreased because of materials agglomeration. However, the decreasing density was dependent on the addition of ZrO₂ particles. The distribution of particles with different volume fractions of mixed particles was investigated by employing SEM, AFM, and EDS tests. Thus, the process can produce a net shape structure that utilises material-bonding consolidation to provide sufficient support to reuse the recovered materials in engineering applications, such as in the automotive industry.