Iron catalysts have been used widely for the mass production of carbon nanotubes (CNTs) with high yield. In this study, UV/visible spectroscopy was used to determine the Fe catalyst content in CNTs using a colorimetric technique. Fe ions in solution form red–orange complexes with 1,10‐phenanthroline, producing an absorption peak at λ=510 nm, the intensity of which is proportional to the solution Fe concentration. A series of standard Fe solutions were formulated to establish the relationship between optical absorbance and Fe concentration. Many Fe catalysts were microscopically observed to be encased by graphitic layers, thus preventing their extraction. Fe catalyst dissolution from CNTs was investigated with various single and mixed acids, and Fe concentration was found to be highest with CNTs being held at reflux in HClO₄/HNO₃ and H₂SO₄/HNO₃ mixtures. This novel colorimetric method to measure Fe concentrations by UV/Vis spectroscopy was validated by inductively coupled plasma optical emission spectroscopy, indicating its reliability and applicability to asses Fe content in CNTs.

High efficiency and mass-scale production ultraviolet (UV) light sources have become a basic requirement for various applications, and as such have attracted considerable technological interest.

This study investigated the effect of graphite nanoplatelet (GNP) size and dispersion on the thermal conductivities and tensile strengths of epoxy-based composites. GNPs of four different platelet sizes, ranging from 1.6 to 3 µm, were derived by mechanically exfoliating and breaking expanded graphite (EG) particles using high-energy bead milling and sonication. The GNPs were used as fillers at loadings of 0–10 wt%. As the GNP size and loading amount increased, the thermal conductivities of the GNP/epoxy composites increased, but their tensile strengths decreased. However, interestingly, the tensile strength reached a maximum value at the low GNP content of 0.3% and thereafter decreased, irrespective of the GNP size. Our observations of the morphologies and dispersions of the GNPs in the composites indicated that the thermal conductivity was more likely related to the size and loading number of fillers, whereas the tensile strength was more influenced by the dispersion of fillers in the matrix.