In order to improve the photocatalytic performance of g-C₃N₄, the g-C₃N₄/Ti₃C₂/Ag₃PO₄ S-type heterojunction catalyst was prepared by electrostatic assembly method, and then the g-C₃N₄/Ti₃C₂/Ag₃PO₄/PAN composite nanofiber membrane was prepared by electrospinning technology. The morphology and chemical properties of the nanofiber membrane were characterized by SEM, FTIR, and XRD, and the photocatalytic degradation of tetracycline hydrochloride (TC) in water by the nanofiber membrane was investigated. The results showed that g-C₃N₄/Ti₃C₂/Ag₃PO₄ could be successfully loaded on PAN and uniformly distributed on the surface of composite nanofiber membrane by electrospinning technology. Increasing the amount of loading and catalyst, lowering the pH value and TC concentration of the system were conducive to the oxidation and degradation of TC. The nano-fiber catalytic membrane had been recycled five times and found to have excellent photocatalytic stability and reusability. The study of catalytic mechanism showed that h⁺, •OH and •O₂⁻ were produced and participated in the oxidation degradation reaction of TC, and •O₂⁻ plays a major role in catalysis. Therefore, this work provides a new insight into the construction of high-performance and high-stability photocatalytic system by electrospinning technology.

Feather and down textiles are widely used in our daily life, especially in winter. However, they are easily drilled out from the fabric body and are difficult to machine-wash, which thereby blocks their widespread application. In order to solve these issues, a highly anti-drilling, breathable and machine-washable ePTFE-aided down-proof cotton fabric was prepared in this work, which was done by modifying a plain-weave cotton fabric with expanded polytetrafluoroethylene (ePTFE) nanofiber membrane via point glue method. The fabrication procedure is simple, scalable and environmentally friendly, which is a prerequisite for large-scale production. The effects of tumble and washing cycles on pore size distribution and the corresponding anti-drilling behavior of the prepared down-proof fabric were systematically investigated. Furthermore, the machine washability, air permeability, thermal insulation and tensile properties of the fabric were studied. The results demonstrated that less than five drilled files escaped from the fabric surface, irrespective of tumble and/or laundering cycles, and it also has the advantages of being lightweight (<83 g/m²), having high breathability, a good thermal insulation rate (≈80%) and can be washed with surfactant by a laundry machine without explosion. Benefiting from the above characteristics, the as-prepared ePTFE-aided down-proof cotton fabric presents its potential application in the field of home textiles.

A scalable approach for manufacturing highly stretchable thermochromic wrapped yarns has been reported previously. Herein, the effects of twist-related technological parameters, namely, wrapping density and outer-inner twist ratio are investigated and have been optimized by technique for order preference by similarity to ideal solution (TOPSIS). The results indicate that the preparatory twist-related parameters have a remarkable effect on the spiral geometrical configuration of yarn constituents, and thus in turn influencing the final tensile and elastic properties of wrapped yarns. The wrapping density of 800 T·m ⁻¹ and outer-inner twist ratio of 1.25 were considered as the optimal alternative using TOPSIS. Moreover, a negative relation between voltage and color-changing time of yarn spun with optimal parameters was established. It was also found that the color of yarn above elevated triggered voltages always switched from purple to pink but followed different color-changing paths. More importantly, thermochromic response of yarn is insensitive to the applied strain.