Clinoptilolite is a natural mineral with exceptional physical characteristics resulting from its special crystal structure, mainstreamed into a large zeolite group called heulandites. An overall view of the research related to the synthesis, modification and application of synthetic clinoptilolite is presented. A single phase of clinoptilolite can be hydrothermally synthesized for 1–10 days in an autoclave from various silica, alumina, and alkali sources with initial Si/Al ratio from 3.0 to 5.0 at a temperature range from 120 to 195 °C. Crystallization rate and crystallinity of clinoptilolite can be improved by seeding. The modification of clinoptilolite has received noticeable attention from the research community, since modified forms have specific properties and therefore their area of application has been broadening. This paper provides a review of the use of organic compounds such as quarter alkyl ammonium, polymer, amine and inorganic species used in the modification process, discusses the processes and mechanisms of clinoptilolite modification, and identifies research gaps and new perspectives.

The microwave-assisted synthesis of goethite nanoparticles has been studied. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), differential thermal analysis (DTA) and Brunauer–Emmett–Teller (BET) method. Goethite rod-like nanoparticles have been successfully synthesized in 10 min of microwave treating at 100 °C. Particle size is in the range from 30 to 60 nm in width and from 200 to 350 nm in length. BET analysis indicated that the surface area of the product is 158.31 m²g⁻¹. The feasibility of Cr(VI) removal fromaqueous solution depends on the pH of the solution and contact time. The maximum adsorptionis reached at pH 4.0 and 540 min of contact time. The adsorption kinetics was analyzedby the pseudo-first- and second-order models and the results reveal that the adsorption process obeys the pseudo-second-order model. The adsorption data were fitted well with the Langmuir adsorption isotherm.