Novel nanoporous film materials of thermostable cyanate ester resins (CERs) were generated by polycyclotrimerization of dicyanate ester of bisphenol E in the presence of varying amounts (from 20 to 40 wt%) of an ionic liquid (IL), i.e., 1-heptylpyridinium tetrafluoroborate, followed by its quantitative extraction after complete CER network formation. The completion of CER formation and IL extraction was assessed using gel fraction content determination, FTIR, 1H NMR, and energy-dispersive X-ray spectroscopy (EDX). SEM and DSC-based thermoporometry analyses demonstrated the formation of nanoporous structures after IL removal from CER networks, thus showing the effective role of IL as a porogen. Pore sizes varied from ~20 to ~180 nm with an average pore diameter of around 45–60 nm depending on the initial IL content. The thermal stability of nanoporous CER-based films was investigated by thermogravimetric analysis.

The polycyclotrimerization reaction of dicyanate ester of bisphenol E (DCBE) in the presence of varying amounts (from 0.5 to 5 wt%) of 1-octyl-3-methylimidazolium tetrafluoroborate ([OMIm][BF4]) ionic liquid has been investigated using differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR) techniques, after a curing stage at 150 °C for 6 h. It is noteworthy that an amount of [OMIm][BF4] as low as 0.5 wt% accelerates dramatically the thermal curing process leading to the formation of a polycyanurate network. The conversion of DCBE increased with increasing [OMIm][BF4] content in the temperature range studied. A reaction mechanism associated with the ionic liquid-catalyzed DCBE polycyclotrimerization is newly proposed via the involvement of a [CN]δ+–[OMIm]δ– complex as a key intermediate