Exceptionally well-preserved three-dimensional insects with fine details and even labile tissues are ubiquitous in the Crato Member Konservat Lagerstätte (northeastern Brazil). Here we investigate the preservational pathways which yielded such specimens. We employed high resolution techniques (EDXRF, SR-SXS, SEM, EDS, micro Raman, and PIXE) to understand their fossilisation on mineralogical and geochemical grounds. Pseudomorphs of framboidal pyrite, the dominant fossil microfabric, display size variation when comparing cuticle with inner areas or soft tissues, which we interpret as the result of the balance between ion diffusion rates and nucleation rates of pyrite through the originally decaying carcasses. Furthermore, the mineral fabrics are associated with structures that can be the remains of extracellular polymeric substances (EPS). Geochemical data also point to a concentration of Fe, Zn, and Cu in the fossils in comparison to the embedding rock. Therefore, we consider that biofilms of sulphate reducing bacteria (SRB) had a central role in insect decay and mineralisation. Therefore, we shed light on exceptional preservation of fossils by pyritisation in a Cretaceous limestone lacustrine palaeoenvironment.

Fe-based materials have extensive applications in the building and automobile industries due to their excellent mechanical properties and low cost. However, their biomedical employment is restricted by the corrosion propensity when in contact with bodily fluids. In this study, single-step Plasma Electrolytic Oxidation, PEO, treatment in Ta-rich electrolyte was used, for the first time, to improve the corrosion resistance of low-carbon steel SAE 1020 for possible use as device implants. The effect of the applied voltage on the chemical and phase composition, topography, wettability, roughness, and corrosion properties were addressed. The results indicated that the Fe-based oxide coatings had a rough and hydrophilic surface, increasing the Ta content with the applied potential. The phase composition of the coatings was mainly composed of hematite (Fe₂O₃), with the Fourier-transform Infrared Spectroscopy, FTIR, spectrums indicating the presence of some absorbed water and organic molecules. The corrosion resistance of the PEO-treated samples was better than the substrate against saline solution (0.9% NaCl) due to the Fe₂O₃ growth decorated with Ta particles, especially the sample treated at 200 V. The results state that Ta-enriched Fe-based oxide coatings could significantly improve the applicability of low-carbon steel SAE 1020 as a low-cost biomaterial, particularly for medical devices.