As the market for polyethylene consumption continues to expand, the amount of waste polyethylene is also increasing. Modifying asphalt with waste polyethylene (PE) is economical and environmentally friendly. The low-temperature performance and storage stability of PE-modified asphalt has long been an insurmountable problem. The high vinyl acetate (VA) content of ethylene–vinyl acetate (EVA) and PE blended into asphalt can improve the compatibility of PE and asphalt. It compensates for the high VA content of EVA brought about by the lack of high-temperature resistance to permanent deformation but is still not conducive to the stable storage of PE at high temperatures. The effect of furfural extraction oil, a crosslinking (DCP) agent, a silicone coupling agent (KH-570), and calcium carbonate (CaCO₃) on the rheological properties and compatibility of PE/EVA-modified asphalt was investigated in this study. The conventional physical properties of PE/EVA-modified asphalt were tested after introducing furfural extraction oil, DCP, KH570, and CaCO₃ to determine the correlations of these materials. In addition, frequency sweep, multiple stress creep and recovery (MSCR), and linear amplitude sweep (LAS) were utilized to characterize the rheological properties and fatigue behavior. The results reveal that the addition of suitable ratios of furfural extract oil, DCP, KH-570, and CaCO₃ to PE/EVA-modified asphalt produces a remarkable improvement in the viscoelastic characteristics and viscosity compared with PE/EVA-modified asphalt. Furthermore, fluorescence microscopy (FM) was utilized to evaluate the modification mechanism, which shows that PE/EVA undergoes significant crosslinking in asphalt, forming a three-dimensional network structure that dissolves in the asphalt. The storage stability of the PE-modified bitumen was fully determined, and its high-temperature rheology was substantially improved.

Three common agricultural beneficial microbes, Trichoderma harzianum, Bacillus cereus, and Pseudomonas fluorescens, are widely used in the growth cycle of crops, and increase the yield of agricultural products through disease prevention and sterilization. As a biodegradable biological macromolecular material, polylactic acid (PLA) is also widely used in agricultural production as a biodegradable film. The addition of agricultural microbes will affect the degradation rate of polylactic acid and thus its agricultural use. Under specific conditions (Tri15), the degradation rate of PLA film exceeds 30%. Scanning electron microscopy (SEM) images show that the degradation of the PLA happened after 360 days of exposure to these three specific microbe environments, which makes the surface of PLA films crack. Gel permeation chromatography (GPC) analysis reveals that in the presence of these microbes, the molecular weight of PLA is reduced. The analysis of 16S rDNA sequences demonstrates that the introduction of these microbes alters the soil microbial community, resulting in an enhanced abundance of Betaproteomicrobes, promoting the degradation of PLA. These results indicate that the three microbes species significantly promote the degradation of PLA, and the effects of microbes vary for the different concentrations. This study establishes practical guidelines for the deployment of PLA in real-world farmland environments.