In recent years, there has been enhanced interest in the domain of natural fibre composites (NFCs) because of their capacity to provide eco-compatible solutions to ever-increasing ecological concerns. This review provides an intensive assessment of the current situation with examination, progress, and applications concerning NFCs. Natural fibres, viz., jute, kenaf, ramie, banana, coir, wheat grass, etc., and their scope in the development of sustainable composites, techniques involved in the fabrication of the composites, characterization techniques, viz., thermo-mechanical and morphological, biodegradability, dampness retention attributes, and potential applications have been extensively reviewed and reported. Besides, this review encompasses the deterrents and conceivable outcomes connected to NFCs, alongside their environmental implications and monetary feasibility. Through a critical evaluation of the existing literature, this article provides a detailed summary of NFCs for real-time engineering applications. It also provides insights into sustainability practices through NFCs.

This study used a hybrid combination of kenaf and hemp fibers and the multi-walled carbon nanotube (MWCNT) reinforcements in the matrix phase to synthesize the composites. A kenaf/hemp fiber blend with MWCNTs in epoxy was used for the specific concentration. The procedure used three composite materials chosen from pilot trials. The ratio of MWCNT filler particles was altered up to the agglomeration limit based on initial trials. Two specimens (2 and 3) were supplemented with MWCNTs in a concentration range of 0.5 wt. % to 1 wt. %, with the fiber concentration being maintained in equilibrium with the epoxy resin, all of the materials were tested under the same conditions. The hybrid nanocomposite was characterized for its morphological and mechanical properties; the tensile properties were higher for 1% MWCNTs concentration (specimen 2), while the flexural properties were higher for 0.5% MWCNTs, with values of 43.24 MPa and 55.63 MPa, correspondingly. Once the MWCNT concentration was increased to 1 wt. %, the maximum impact strength was achieved (specimen 3). In the limits of the Shore-D scale, the kenaf fiber and hemp fiber matrix composite (specimen 1) gained a hardness index of 84. Scanning electron microscopy was carried out to analyze the morphological features of the fractured samples and to assess the adhesion between the fiber, matrix, and surface. Among the various fillers tested, the kenaf fiber/hemp/MWCNT composite (specimen 3) demonstrated superior binding and reduced the incidence of fiber pull-out, breakage, and voids. In addition to the comparative analysis, the addition of 0.5 wt. % MWCNTs resulted in better mechanical properties compared to the other two combinations.

This study explores the impact of fly ash (FA) filler on the mechanical, morphological, and water absorption properties of pineapple leaf fibre (PALF)-reinforced epoxy composites for biomedical applications.

The choice of suitable inoculants in the grain refinement process and subsequent enhancement of the characteristics of the composites developed is an important materials research topic, having wide scope. In this regard, the present work is aimed at finding the appropriate composition and size of fly ash as inoculants for grain refinement of the aluminum AA 5083 composites. Fly ash particles, which are by products of the combustion process in thermal power plants, contributing to the large-scale pollution and landfills can be effectively utilized as inoculants and interatomic lubricants in the composite matrix–reinforcement subspaces synthesized in the inert atmosphere using ultrasonic assisted stir casting setup. Thus, the work involves the study of the influence of percentage and size of the fly ash dispersions on the tensile and impact strength characteristics of the aluminum AA 5083/7.5SiC composites. The C type of fly ash with the particle size in the series of 40–75 µm, 76–100 µm, and 101–125 µm and weight % in the series of 0.5, 1, 1.5, 2, and 2.5 are selected for the work. The influence of fly ash as distinct material inoculants for the grain refinement has worked out well with the increase in the ultimate tensile strength, yield strength, and impact strength of the composites, with the fly ash as material inoculants up to 2 wt. % beyond which the tensile and impact characteristics decrease due to the micro coring and segregation. This is evident from the microstructural observations for the composite specimens. Moreover, the role of fly ash as material inoculants is distinctly identified with the X-Ray Diffraction (XRD) for the phase and grain growth epitaxy and the Energy Dispersive Spectroscopy (EDS) for analyzing the characteristic X-Rays of the fly ash particles as inoculant agents in the energy spectrum.

Natural fiber-reinforced polymer composite is a rapidly growing topic of research due to the simplicity of obtaining composites that is biodegradable and environmentally friendly. The resulting composites have mechanical properties comparable to synthetic fiber-reinforced composites. In this regard, the present work is formulated with the objectives related to the development, characterization, and optimization of the wt of reinforcements and the process parameters. The novelty of this work is related to the identification and standardization of the appropriate wt of reinforcements and parameters for the processing of the areca nut leaf sheath fiber-based polymer composites for enhanced performance attributes. With this basic purview and scope, the composites are synthesized using the hand layup process, and the composite samples of various fiber compositions (20, 30, 40, and 50) are fabricated. The mechanical characteristics of biodegradable polymer composites reinforced with areca nut leaf sheath fibers are investigated in the present work, with a focus on the effect of fiber composition (tensile properties, flexural strength, and impact strength). The properties of composites are enhanced by combining the areca nut leaf sheath fiber and epoxy resin, with a fiber content of 50 being the optimal wt. The Scanning electron microscopy (SEM) investigations also ascertain this by depicting the good interfacial adhesion between the areca nut leaf sheath fiber and the epoxy resin. The tensile strength of the composite specimen reinforced with 50 areca nut fiber increases to 44.6MPa, while the youngs modulus increases to 1900MPa, flexural strength increases to 64.8MPa, the flexural modulus increases to 37.9GPa, and impact strength increases to 34.1kJ/m². As a result, the combination of areca nut leaf sheath fiber reinforced epoxy resin shows considerable potential as a renewable and biodegradable polymer composite. Furthermore, areca nut leaf sheath fiber-reinforced epoxy resin composites are likely to replace petroleum-based polymers in the future. The ecosustainability and biodegradability of the composite specimen alongside the improved mechanical characteristics serve as the major highlight of the present work, and can help the polymer composite industry to further augment the synthetic matrix and fiber-based composites with the natural fiber-reinforced composites.