Dental pulp stem cells (DPSCs) play a crucial role in the tissue healing process through odontoblast like cell differentiation. The aim of this study was to evaluate the biocompatibility and compare the potential invitro cytotoxic effects of NeoMTA Plus, ProRootMTA and Biodentine on human dental pulp stem cells (hDPSCs). To assess the effects of NeoMTA Plus, ProRoot MTA and Biodentine extracts at 1st, 3rd and 7th d on hDPCs, cell populations was determined by flow cytometry using an Annexin V detection kit. The data were analyzed statistically using the Kruskal–Wallis test. A p < 0.05 was considered as statistically significant. All groups showed cell viability similar to that of the control group on 1st, 3rd and 7th d. Although Biodentine exhibited higher cell viability rates than the other material groups, no statistically significant differences were noted between the sampled days (p > 0.05). All materials extracts are not cytotoxic and do not induce apoptosis in the hDPSCs. These results suggest that all the tested materials can lead to positive outcomes when used as reparative biomaterials.

Background: This study aimed to evaluate possible cytotoxic effects to gingival epithelial cells exposed to children toothpastes containing different detergent. Methods: Tissues required for the isolation of human gingival epithelial cells were obtained by biopsy during the extraction of the impacted third molar tooth. Toothpaste solutions of different concentrations were prepared from five different children’s toothpastes with different detergent contents. Isolated gingival epithelial cells were stimulated with experimental groups consisting of toothpaste solutions (Colgate, Sensodyne, Splat, Nenedent, Perlodent) at different concentrations and a control group consisting of complete Dulbecco’s modified eagle medium. After the experiments, cell viability was evaluated using flow cytometry. 2 Way ANOVA was used to see the interaction effect of the main effects of toothpaste solution and concentration factors. Pairwise comparisons were made by Tukey post hoc tests. In the study, the significance level was taken as 0.05. Results: As a result of the analysis, it was seen that the toothpaste solution and concentration factors and the interactions of these 2 factors were effective on the viable, early apoptotic, late apoptotic and necrotic cell rates. The statistically highest live cell ratios were detected in Splat’s toothpaste solutions (90.14% at 0.4% concentration) after the control group (90.82%) and the group with the lowest viability values was determined in Colgate group (75.74% at 0.4% concentration) (p < 0.05). Conclusions: According to the results of the study, it was observed that toothpastes containing SLS affected the viability of cells more negatively than toothpastes with other detergent contents.

Objectives This study aimed to determine the knowledge and approaches of the participants about oral and dental health. Materials and Methods This was a questionnaire-based cross-sectional survey. Participants’ demographic characteristics, tooth brushing habits, selection of toothpaste, and reasons for visiting the dentist were examined in this study. Participants’ knowledge levels of fluoride and their attitudes toward the most common fluoride applications among preventive treatments were also evaluated. Data entry and analyses were performed using SPSS statistical software. Descriptive and inferential statistics and chi-square test were used for analyzes. Results A total of 2,744 voluntary participants including 1,938 (70.6%) females and 806 (29.4%) males responded; 1,391 (50.7%) participants know the contents of their toothpaste; 1,680 (61.2%) participants point out that fluoride is effective in preventing dental caries. Female participants reported a statistically significant difference in their knowledge of what is fluoride when compared with male participants (p = 0.0001). The knowledge level of participants who had higher levels of education were statistically significantly different when compared with the participants who had lower education levels about fluoride and fluoride applications (p = 0.0001). Conclusions The results of this study indicate that participants’ attitudes toward oral health and dental care need to be improved.

The aim of this study is to evaluate the surface microhardness, surface chemical composition of bioactive restorative materials pre- and post- thermal aging. A total of 200 disc-shaped samples were prepared by using the materials: Cention N, ACTIVA BioActive Restorative, Equia Forte HT Fil, Glass Fill glass carbomer cement (GCP), and Fuji II LC. Vickers microhardness test were used to measure surface hardness. Scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM/EDS) was used to determine the characterization of the microstructures and elemental analysis of the materials. These measurements were repeated after thermal aging. One-Way ANOVA test, Bonferroni test and the Games-Howell test was used for data analysis. The significance level was accepted as 0.05. Cention N had the highest vickers microhardness value before thermal cycle. The highest fluoride ion ratio among the materials before thermal aging was detected in the Equia Forte HT Fil and Fuji II LC groups. While a decrease in fluorideF ion was detected in all groups except the Cention N group after thermal aging. It is observed that ACTIVA BioActive Restorative has a more microporous and rougher surface in the scanning electron microscopy image after the thermal cycle than in the image before the thermal cycle. The chemical properties of the materials and the properties of the filler particles may be related to the differences in the mechanical properties, surface characterizations and ion releases of the materials Thermal aging affected the microhardness, surface characteristics and elemental mass ratios of the studied materials. Alkasite bioactive materials are more similar to composite restorative materials and show better mechanical properties than other materials, but do not have the same effect on fluoride release. Most of the bioactive materials showed a decrease in the fluoride ion ratio after thermal aging, while no difference was found in the ion exchange of alkasite materials. Material selection should be made more carefully in caries-active individuals whose fluoride release is clinically important.

The purpose of this in vitro study was to assess the color stability of esthetic restorative materials after immersion in different pediatric drugs. Three different restorative materials namely composite resin, alkasite and high-viscosity glass ionomer cement(HVGIC) were used to prepare total 96 (32 from each) disc-shaped specimens(2mmx5mm). A spectrophotometer was used to record the color of each sample after sample preparation and 7 days following the staining technique. After 1-week period, ΔE ∗ values were calculated. The average color changes(ΔE) for all drugs/restorative materials ranged from 1.81 to 8.08. The most prominent alteration was found in Cough syrup-Alkasite(8.08 ± 2.62) and the least one was found in Cough syrup-HVGIC(1.81 ± 0.74) pairwise. The color change observed in Cough syrup-Alkasite group was statistically significantly higher than in Cough syrup-HVGIC (p < 0.05). Alkasite showed greater color alteration with all drugs compared to other materials and HVGIC showed better color stability with all drug formulations.

There are recent studies which aimed to detect the inheritance on the etiology of dental caries exploring oral composition. We present data on the oral microbiota and its relation with dental caries and other factors in monozygotic (MZ) and dizygotic (DZ) twin children. Following clinical investigation, DNA samples were collected and isolated from saliva of 198 patients (49 MZ and 50 DZ twins) with an average age of 9.7 ± 2.7 years. Salivary bacterial microbiota analysis was performed using high throughput amplicon sequencing method targeting V3-V4 region of the 16S rRNA gene. A total of 8,297,859 raw reads corresponding to 41,908 reads per sample were obtained on average. The QIIME2-deblur workflow was used for 16S rRNA amplicon analysis. Microbiome similarity analyses between twins (based on Bray-Curtis dissimilarity, weighted and unweighted Unifrac distances) showed that monozygotic twins share more bacterial microbial content compared to dizygotic twins. This is a large microbial community dataset of MZ and DZ twins with or without dental findings which can be further used for children oral microbiome profile explorations.