In this work, we demonstrate the surface functionalization of cellulose triacetate membrane with co-deposition of polydopamine (PDA)/polyethyleneimine (PEI) and silver nanoparticles (AgNPs) for antifouling property in municipal wastewater treatment. PDA/PEI was first coated on the membrane surface by single-step co-deposition, while AgNPs were formed in situ through catechol groups of PDA immobilizing silver ions and subsequently reducing. The successful surface modification was verified by different membrane characterization techniques. The modified PDA/PEI-nAg CTA membrane exhibits enhanced hydrophilicity and improved antiadhesion and antimicrobial activity. Furthermore, the functional layer had an indistinctive effect on the membrane transport parameters. In addition, dynamic forward osmosis (FO) fouling experiment with raw municipal wastewater as feed solution indicated that the PDA/PEI-nAg CTA membrane exhibited notably lower water flux decrease compared to the nascent CTA membrane. The results of confocal laser scanning microscopy (CLSM) showed that PDA/PEI-nAg CTA membranes effectively reduced the adsorption of organic foulants (proteins and polysaccharides) and inhibited the formation and development of the fouling layer. The membrane surface modification of the CTA membrane with PDA/PEI and AgNPs efficiently mitigated membrane fouling in municipal wastewater treatment.

In this study, a multi-functional layer was developed based on the commercially available cellulose triacetate (CTA) forward osmosis (FO) membrane to improve its antifouling property. Tannic acid/ferric ion (TA/Fe3+) complexes were firstly coated as a precursor layer on the membrane surface via self-assembly. Afterwards, the tannic acid/diethylenetriamine (TA/DETA) hydrophilic functional layer was further coated, following Ag/polyvinylpyrrolidone (PVP) anti-bacterial layer was formed in situ through the reducibility of TA to obtain TA/Fe3+-TA/DETA-Ag/PVP-modified membrane. The optimized precursor layer was acquired by adjusting the buffer solution pH to 8, TA/Fe3+ ratio to 4 and the number of self-assembled layers to 5. The permeability testing results illustrated that the functional layer had an insignificant effect on the membrane transport parameters. The TA/Fe3+-TA/DETA-Ag/PVP-modified membrane simultaneously exhibited excellent physical and chemical stability. The coated membrane also demonstrated enhanced anti-bacterial properties, achieving 98.63 and 97.30% inhibition against Staphylococcus aureus and Escherichia coli, respectively. Furthermore, the dynamic fouling experiment showed a 12% higher water flux decrease for the TA/Fe3+-TA/DETA-Ag/PVP CTA membrane compared to the nascent CTA membrane, which proved its excellent antifouling performance. This work provides a feasible strategy to heighten the antifouling property of the CTA FO membrane.