We prepared different PtSnX (X = Ni, Ru, Rh, Pd, and W) nanocatalysts supported on Vulcan carbon XC-72 with 40 wt% metal loading by thermal decomposition of polymeric precursors (DPP) and tested their activity in the electrooxidation of ethanol in acidic medium (0.05 mol L⁻¹ H₂SO₄). We characterized the nanoparticles by EDX and XRD, which revealed 64% atomic ratio of Pt in an fcc structure with crystallite sizes of 4 to 10 nm. Electrochemical tests in the presence of ethanol showed that the addition of Ni to the PtSn/C nanocatalysts enhanced ethanol electrooxidation. The composition Pt₆₆Sn₁₁Ni₂₃/C presented mass activity of 3.5 A g_Pt⁻¹ and power density of 25 mW cm⁻² in a direct ethanol fuel cell test. The Ni effect on the PtSn nanocatalyst prompted us to synthesize and test other compositions containing this metal and use them in a direct ethanol fuel cell station. The Pt₈₂Sn₀₉Ni₀₉/C nanocatalyst delivered the best power density value (45 mW cm⁻²).

We have investigated platinum catalysts containing iron as a modifier to obtain catalysts with superior electrocatalytic activity toward glycerol electro-oxidation in an alkaline medium. The electrocatalysts, supported on carbon Vulcan, were synthesized by the polyol method. The physicochemical characterization data showed that the metals were well distributed on the carbon support and had small particle size (2 nm). The Pt:Fe metal ratio differed from the nominal composition, indicating that reducing iron with platinum was difficult, even though some parameters of the synthesis process were changed. Electrochemical analyses revealed that PtFe/C was more active and stable than commercial Pt/C was, and analysis of the electrolysis by-products showed that iron addition to Pt/C boosted the glycerol conversion and selectivity for glyceric acid formation.