Two experimental techniques—time domain spectroscopy (TDS) and a steady state frequency method—have been used to study dielectric spectra for the isotropic, nematic, S_A, S_C and S_Y phases of two thioesters (4-n-pentylphenyl-4′-n-octyloxy-and 4′-n-nonyloxythiobenzoates (C _n H_2n+1 O‒C₆ H₄‒COS‒C₆H₄‒C₅H₁₁, where n = 8 and n = 9) known as 8S5 and 9S5, in the frequency range from 10 Hz to 10 GHz. In the case of 8S5 a deuteriated sample (8S5-d ₂₈) has been used to study relaxation processes in the nematic and smectic phases.

In this research, the cold spray process as an additive manufacturing method was applied to deposit thick titanium coatings onto 7075 aluminium alloy. An analysis of changes in the microstructure and mechanical properties of the coatings depending on the standoff distance was carried out to obtain the maximum deposition efficiency. The process parameters were selected in such a way as to ensure the spraying of irregular titanium powder at the highest velocity and temperature and changing the standoff distance from 20 to 100 mm. Experimental studies demonstrated that the standoff distance had a significant effect on the microstructure of the coatings and their adhesion. Moreover, its rise significantly increased the deposition efficiency. The standoff distance also significantly affected the coating microstructure and their adhesion to the substrate, but did not cause any changes in their phase composition. The standoff distance also influenced the coating porosity, which first decreased to a minimum level of 0.2% and then increased significantly to 9.8%. At the same time, the hardness of the coatings increased by 30%. Numerical simulations confirmed the results of the tests.

Corrosion resistance of the cold-sprayed nickel coatings deposited on the Ni surface (substrate) without and with abrasive grit-blasting treatment of the substrate was investigated. The corundum powder with different grain sizes was used. The corrosive environment contained an acidic chloride solution. The mechanism of the corrosion of nickel was suggested and discussed. Corrosion electrochemical parameters were determined by electrochemical methods. The corrosion effect of a nickel coating depends on the grain size used to prepare the substrate. The nickel coating after the medium grit-blasting treatment of the substrate was found to be the most corrosion resistant. However, the smallest resistance on the corrosion effect should be attributed to the nickel coating on the substrate after the coarse grit-blasting treatment.

In this work, the high frequency dielectric relaxation process has been studied for the N*, S*_A and S*_C phases of the mixture ZLI 3654. To this end, time domain spectroscopy (TDS) was used to cover the frequency range from 10⁷ to 10¹⁰ Hz. The dielectric parameters obtained show that the high frequency spectrum is mostly influenced by the reorientation of molecules around their long axes. In addition, the latter process seems to be strongly hindered in the S*_C phase, because the necessary relaxation time is of the order of 1 ns, whereas for the N* and S*_A phases, the relaxation time is remarkably shorter and equal to 0.3 and 0.4 ns, respectively.

Nanostructured and composite WC-12Co coatings were prepared by means of the supersonic spray process (HVOF). The microstructure and composition of WC-12Co nanostructured powder were analyzed by scanning electron microscope (SEM) and transmission electron microscope (TEM). Investigations revealed nano grains of WC with the size in the range of 50-500 nm. The nanostructured sprayed coating was analysed by SEM and phase composition was investigated by X-ray diffractometer (XRD). A denser coating structure with higher hardness was observed compared to conventional coating with a small amount of W₂C, WC_1−x, W and some amorphous phase. Young’s modulus and hardness were determined by depth sensing indentation in HVOF sprayed WC-12Co nanostructured coatings. Results were compared to conventional coatings and the relevance of the nanostructure was analyzed. An indentation size effect was observed on the polished surface and cross-section of both coatings. Data provided by indentation tests at maximum load allow to estimate hardness and elastic modulus. Enhanced nanomechanical properties of conventional coating in comparison to nanostructured one were observed. Nanostructured coatings WC-12Co (N) revealed significantly better corrosion resistance.