The heating and cooling profiles experienced during laser additive manufacturing results in residual stresses build up in the component. Therefore, it is necessary to perform post build stress relieving towards the retention and improvement of the mechanical properties. However the thermal treatments for conventional manufacturing do not seem to completely accommodate these rapid heating and cooling cycles of laser processing techniques such as powder bed fusion. Characterizations such as density measurements on the samples were performed employing the Archimedes principle; hardness testing was performed on the Zwick micro/macro (Hv) hardness tester, SEM and Electron backscatter diffraction (EBSD). Fracture toughness and crack growth was conducted on a fatigue crack machine. All characterization was done after stress relieving of Selective Laser Melting (SLM) produced samples at 300 °C for 2 hrs was performed in a furnace. The mechanical properties appear to be rather compromised instead of being enhanced desirably. As-built SLM produced tensile specimens built in different directions exhibited significantly favorable mechanical properties. However, post stress relieve thermal treatment technique deteriorated the strength while increasing the ductility significantly. Nonetheless, fatigue crack growth and fracture toughness illustrated positive outcome in terms of fatigue life on SLM produced AlSi10Mg components in application.

This study investigates effect of different concentrations of ethylenediaminetetraacetic disodium dihydrate (EDTA-Na₂: C₁₀H₁₄N₂Na₂O₈.2H₂O) and sodium nitrite (NaNO₂) admixtures, individually or in synergistic/partial NaNO₂ replacement model, on the corrosion of concrete steel-rebar in NaCl and in H₂SO₄ media. Electrochemical monitoring techniques were employed for 48 steel-reinforced concrete samples immersed in the saline/marine and microbial/industrial simulating test environments for 96 days. These test data were subjected to the analyses of the Normal and the Weibull distribution fitting models, for each of which goodness of their fitting the electrochemical test data were studied using the Kolmogorov–Smirnov test statistics. Analysed results showed that EDTA-Na₂ admixture concentrations exhibited better inhibition effectiveness, with relatively good effectiveness in their synergistic admixtures, than their equal-mass NaNO₂ counterparts in both corrosive environments. Also, post-electrochemical experiment subjection of the concrete samples to testing and analyses of ASTM C39/C39M-03 and ASTM C267-01 showed that use of the optimally inhibiting 8 g EDTA-Na₂ (per 2 × 10^–3m³ concrete) culminates in gross reduction in compressive strength of concretes in both test-media. However, lowered EDTA-Na₂ concentrations exhibited better strength improvements with high corrosion inhibition in the test environments. These suggest suitability of EDTA-Na₂ as an environmental-friendly NaNO₂ alternative for inhibiting steel-rebar corrosion in saline/marine and microbial/industrial environments.

The NiTi intermetallic possesses a number of good properties, such as high wear, oxidation, and corrosion resistance. This paper focuses on the deposition of NiTi intermetallic coatings on Ti6Al4V substrate by laser melting of Ti and Ni elemental powder mixtures. The effect of varying the Ti content in the NiTi composition on the microstructure and wear properties of the coatings was investigated. The microstructure of the NiTi intermetallic coatings were characterized by the scanning electron microscope (SEM) equipped with Energy Dispersive Spectroscope (EDS). The wear properties of the coatings were performed under accelerated dry sliding wear tests. The results obtained from the SEM/EDS analysis; show that the coatings consist of Ni and Ti elements from the feedstock, and the NiTi, NiTi₂and NiTi₃, intermetallic phases. Dry sliding wear analysis revealed that there is correlation between the hardness and the wear rate. The coatings displayed significant improvement in wear resistance up to 80% compared to the substrate.

This data article details Pseudomonas aeruginosa effects on the bioremediation of soil that had been polluted by different concentrations, 5% w/w and 8% w/w, of raw (for simulating oil spills from well-heads) and treated (for simulating oil spills from flow lines/storage tanks) crude oil. UV/VIS spectrophotometry instrumentation was used for obtaining absorbance measurements from the Nigerian Escravos Light blend (sourced from Chevron® Nigeria) of crude oil polluting soil samples, which, thus, also simulates light and heavy onshore oil spillage scenarios, in a 30-day measurement design. Data on bioremediation effects of Pseudomonas aeruginosa added to the crude oil polluted soil samples, and which were monitored at intervals via the absorbance measurement techniques, are presented in tables with ensuing analyses for describing and validating the data presented in graphs. Information from the presented data in this article is useful to researchers, the oil industries, oil prospecting communities, governments and stakeholders involved in finding solution approach to the challenges of onshore oil spills. This information can also be used for furthering research on bioremediation kinetics such as biostimulant analyses, polluting hydrocarbon content/degradation detailing, by Pseudomonas aeruginosa strain of microorganism, on petroleum pollutant removal from soil that had been polluted by crude oil spillage.