Osteolysis due to wear of UHMWPE limits the longevity of joint arthroplasty. Oxidative degradation of UHMWPE gamma-sterilized in air increases its wear while decreasing mechanical strength. Vitamin E stabilization of UHMWPE was proposed to improve oxidation resistance while maintaining wear resistance and fatigue strength. We reviewed the preclinical research on the development and testing of vitamin E-stabilized UHMWPE with the following questions in mind: (1) What is the rationale behind protecting irradiated UHMWPE against oxidation by vitamin E? (2) What are the effects of vitamin E on the microstructure, tribologic, and mechanical properties of irradiated UHMWPE? (3) Is vitamin E expected to affect the periprosthetic tissue negatively? We performed searches in PubMed, Scopus, and Science Citation Index to review the development of vitamin E-stabilized UHMWPEs and their feasibility as clinical implants. The rationale for using vitamin E in UHMWPE was twofold: improving oxidation resistance of irradiated UHMWPEs and fatigue strength of irradiated UHMWPEs with an alternative to postirradiation melting. Vitamin E-stabilized UHMWPE showed oxidation resistance superior to that of irradiated UHMWPEs with detectable residual free radicals. It showed equivalent wear and improved mechanical strength compared to irradiated and melted UHMWPE. The biocompatibility was confirmed by simulating elution, if any, of the antioxidant from implants. Vitamin E-stabilized UHMWPE offers a joint arthroplasty technology with good mechanical, wear, and oxidation properties. Vitamin E-stabilized, irradiated UHMWPEs were recently introduced clinically. The rationale behind using vitamin E and in vitro tests comparing its performance to older materials are of great interest for improving longevity of joint arthroplasties.

Ultra-high molecular weight polyethylene (UHMWPE) is the most common bearing material in total joint arthroplasty due to its unique combination of superior mechanical properties and wear resistance over other polymers. A great deal of research in recent decades has focused on further improving its performances, in order to provide durable implants in young and active patients. From “historical”, gamma-air sterilized polyethylenes, to the so-called first and second generation of highly crosslinked materials, a variety of different formulations have progressively appeared in the market. This paper reviews the structure–properties relationship of these materials, with a particular emphasis on the in vitro and in vivo wear performances, through an analysis of the existing literature.

Wear debris related osteolysis is recognised as being the main cause of failure in joint replacements based on UHMWPE inserts. However, many solutions and “new” polyethylenes have been suggested in order to address this issue. This review discusses “historical” issues associated with UHMWPE, such as oxidation, sterilization method and storage, as well as “new” topics, such as crosslinking and stabilization. The final aim is to aid orthopaedic surgeons in their selection of polyethylene inserts and in the information given to the patients. The main problem for the polymer is degradative oxidation, which is caused by the combination of the irradiation used for sterilization and oxygen, and which leads to a decrease in wear resistance and mechanical properties. Irradiation and packaging in the absence of oxygen can only reduce the oxidation, while sterilization with gas (EtO or gas plasma) is the only method that effectively eliminates it. Manufacturing processes are of great relevance to the clinical duration and must be considered by surgeons. Crosslinked polyethylene has been developed for joint inserts due to its superior wear resistance compared to conventional UHMWPE; to prevent the oxidation, crosslinked polyethylene requires post-irradiation thermal treatment, which reduces its mechanical properties and which depends on the producer. Several good clinical results from the use of crosslinked acetabular cups have reported at mid-term, while early results for knee replacements are also encouraging. Recently, the use of the antioxidant vitamin E (alpha-tocopherol) has been introduced for joint prostheses in order to prevent the oxidation of both crosslinked and noncrosslinked UHMWPE.