The rapid drop in internal temperature of mass concrete can readily lead to temperature cracks. Hydration heat inhibitors reduce the risk of concrete cracking by reducing the temperature during the hydration heating phase of cement-based material but may reduce the early strength of the cement-based material. Therefore, in this paper, the influence of commercially available hydration temperature rise inhibitors on concrete temperature rise is studied from the aspects of macroscopic performance and microstructure characteristics, and their mechanism of action is analyzed. A fixed mix ratio of 64% cement, 20% fly ash, 8% mineral powder and 8% magnesium oxide was used. The variable was different admixtures of hydration temperature rise inhibitors at 0%, 0.5%, 1.0% and 1.5% of the total cement-based materials. The results showed that the hydration temperature rise inhibitors significantly reduced the early compressive strength of concrete at 3 d, and the greater the amount of hydration temperature rise inhibitors, the more obvious the decrease in concrete strength. With the increase in age, the influence of hydration temperature rise inhibitor on the compressive strength of concrete gradually decreased, and the decrease in compressive strength at 7 d was less than that at 3 d. At 28 d, the compressive strength of the hydration temperature rise inhibitor was about 90% in the blank group. XRD and TG confirmed that hydration temperature rise inhibitors delay early hydration of cement. SEM showed that hydration temperature rise inhibitors delayed the hydration of Mg(OH)₂.

Using the volume expansion generated by the hydration of the MgO expansive agent to compensate for the shrinkage deformation of concrete is considered to be an effective measure to prevent concrete shrinkage and cracking. Existing studies have mainly focused on the effect of the MgO expansive agent on the deformation of concrete under constant temperature conditions, but mass concrete in practical engineering experiences a temperature change process. Obviously, the experience obtained under constant temperature conditions makes it difficult to accurately guide the selection of the MgO expansive agent under actual engineering conditions. Based on the C50 concrete project, this paper mainly investigates the effect of curing conditions on the hydration of MgO in cement paste under actual variable temperature conditions by simulating the actual temperature change course of C50 concrete so as to provide a reference for the selection of the MgO expansive agent in engineering practice. The results show that temperature was the main factor affecting the hydration of MgO under variable temperature curing conditions, and the increase in the temperature could obviously promote the hydration of MgO in cement paste, while the change in the curing methods and cementitious system had an effect on the hydration of MgO, though this effect was not obvious.