One of the most important measures implemented to reduce SARS-CoV-2 transmission has been the use of face masks. Yet, most mask options available in the market display a passive action against the virus, not actively compromising its viability. Here, we propose to overcome this limitation by incorporating antiviral essential oils (EOs) within polycaprolactone (PCL) electrospun fibrous mats to be used as intermediate layers in individual protection masks. Twenty EOs selected based on their antimicrobial nature were examined for the first time against the Escherichia coli MS2 virus (potential surrogate of SARS-CoV-2). The most effective were the lemongrass (LGO), Niaouli (NO) and eucalyptus (ELO) with a virucidal concentration (VC) of 356.0, 365.2 and 586.0 mg/mL, respectively. PCL was processed via electrospinning, generating uniform, beadless fibrous mats. EOs loading was accomplished via two ways: (1) physisorption on pre-existing mats (PCLaEOs), and (2) EOs blending with the polymer solution prior to fiber electrospinning (PCLbEOs). In both cases, 10% v/v VC was used as loading concentration, so the mats’ stickiness and overwhelming smell could be prevented. The EOs presence and release from the mats were confirmed by UV-visible spectroscopy (≈5257–631 µg) and gas chromatography-mass spectrometry evaluations (average of ≈14.3% EOs release over 4 h), respectively. PCLbEOs mats were considered the more mechanically and thermally resilient, with LGO promoting the strongest bonds with PCL (PCLbLGO). On the other hand, PCLaNO and PCLaELO were deemed the least cohesive combinations. Mats modified with the EOs were all identified as superhydrophobic, capable of preventing droplet penetration. Air and water-vapor permeabilities were affected by the mats’ porosity (PCL < PCLaEOs < PCLbEOs), exhibiting a similar tendency of increasing with the increase of porosity. Antimicrobial testing revealed the mats’ ability to retain the virus (preventing infiltration) and to inhibit its action (log reduction averaging 1). The most effective combination against the MS2 viral particles was the PCLbLGO. These mats’ scent was also regarded as the most pleasant during sensory evaluation. Overall, data demonstrated the potential of these EOs-loaded PCL fibrous mats to work as COVID-19 active barriers for individual protection masks.

Non-invasive glucose determination provides major advantages in health monitoring and protection. It enables widespread point-of-care testing, which is affordable, sensitive, specific, rapid and equipment-free. This work reports on the development and analytical performance of a colorimetric biosensor in detecting glucose in human urine. Highly porous polyamide microparticles were synthesized as the support for the glucose oxidase (GOx) and horseradish peroxidase (HRP) dyad, which was immobilized randomly or consecutively—first HRP and then GOx. The latter system was superior, as GH@PA-C showed much higher activity than the random system, and it was used to prepare the biosensor, along with the 3,3′,5,5′-tetramethylbenzidine chromogen. When in contact with urine, the biosensor displayed a strict linear correlation between the color difference and the glucose concentration in urine in the range of 0.01–3.0 mM, as established by the CIELab image processing algorithm and UV-VIS measurements. The biosensor acted in 20 s and had a detection limit of 30.7 µM in urine, high operational activity at pH = 4–8 and unchanged detection performance after 30 days of storage. Its unique feature is the possibility of multiple consecutive uses without the serious deterioration of the recovery and dispersion values. These characteristics can open the way for new routines in non-invasive personal diabetes detection.

Anterior cruciate ligament (ACL) injuries pose significant challenges, driving the need for innovative repair strategies. Tissue engineering (TE) has emerged as a promising field for ACL injuries. Wet spinning is a filament production technique that enables precise control over filament alignment, diameter, and porosity, making it suitable for developing new scaffolds for ACL injuries. This study develops fibrous scaffolds using wet spinning of polycaprolactone (PCL) reinforced with cellulose nanocrystals (CNC) to enhance mechanical properties. Wet spinning was employed to fabricate fibrous scaffolds, utilizing PCL as the primary polymer due to its favorable biocompatibility and degradability. An automated collector was developed and optimized, which allowed the stretching of the PCL filaments to diameters as low as 30 µm. Several filaments were explored and characterized using SEM, TGA, and mechanical tests. The optimized PCL/CNC filaments were used to develop 3D braided structures that mimic ACL structure. The combination of wet-spun PCL/CNC filaments (with an optimized stirring method) and the braiding procedure allowed for fully biocompatible scaffolds that mimic both the structure and the mechanical properties of native ACL. Cytotoxicity and biocompatibility tests showed cell viability and proliferation values above 99% and 81%, respectively. These findings underscore the potential of CNC-reinforced PCL scaffolds as promising candidates for ACL repair, laying the groundwork for future biomedical applications.