Gold nanoparticles are widely used in laser biomedical applications due to their favorable properties, mainly localized plasmon resonance. However, laser radiation can cause a change in the shape and size of plasmonic nanoparticles, thus resulting in an unwanted reduction of their photothermal and photodynamic efficiency due to a drastic alteration of optical properties. Most previously reported experiments were carried out with bulk colloids where different particles were irradiated by different numbers of laser pulses, thus making it difficult to accurately evaluate the laser power photomodification (PM) threshold. Here, we examine the one-shot nanosecond laser-pulse PM of bare and silica-coated gold nanoparticles moving in a capillary flow. Four types of gold nanoparticles, including nanostars, nanoantennas, nanorods, and SiO₂@Au nanoshells, were fabricated for PM experiments. To evaluate the changes in the particle morphology under laser irradiation, we combine measurements of extinction spectra with electron microscopy. A quantitative spectral approach is developed to characterize the laser power PM threshold in terms of normalized extinction parameters. The experimentally determined PM threshold increases in series were as follows: nanorods, nanoantennas, nanoshells, and nanostars. An important observation is that even a thin silica shell significantly increases the photostability of gold nanorods. The developed methods and reported findings can be useful for the optimal design of plasmonic particles and laser irradiation parameters in various biomedical applications of functionalized hybrid nanostructures.

Gold nanostars with an average core diameter of 122,2 nm and a spike length of 114,6 nm were synthesized and characterized at a concentration of 5,36×1010 pcs/ml with an absorption maximum of 840 nm. Gold nanostars were coated with thiolated polyethylene glycol, its amount was about 8×104 molecules per 1 particle and about 4,4×1015 molecules/ml in the colloid. The zeta potential of gold nanostars coated with PEG-SH was −2.3 mV. The combined effect of gold nanostars and low-intensity infrared (808 nm) laser radiation on the bacteria Staphylococcus aureus 209 P and Escherichia coli 113-13 has been studied. Incubation of suspensions of microorganisms in the presence of nanoparticles without access to light did not lead to a significant reduction in the number of bacteria. Irradiation for 30 min of bacterial suspensions containing nanoparticles caused the death of 39% of the S. aureus population and 80% of the E. coli population. During the thermometry of the studied suspensions, it was found that the temperature increase is dose-dependent. The increase in temperature of the control samples that did not contain photothermal agents did not exceed 1 °C in both cases throughout the entire time of the experiment. For suspensions of bacteria (equally S. aureus and E. coli) incubated with gold nanostars during irradiation, an increase in temperature indicators, on average, by 4 °C was revealed. The more pronounced antibacterial activity of the combination of gold nanostars and infrared (808 nm) laser radiation against E. coli can also be explained by the greater sensitivity of gram-negative microorganisms to photothermal exposure.