Industry 4.0 in healthcare involves use of a wide range of modern technologies including digitisation, artificial intelligence, user response data (ergonomics), human psychology, the Internet of Things, machine learning, big data mining, and augmented reality to name a few. The healthcare industry is undergoing a paradigm shift thanks to Industry 4.0, which provides better user comfort through proactive intervention in early detection and treatment of various diseases. The sector is now ready to make its next move towards Industry 5.0, but certain aspects that motivated this review paper need further consideration. As a fruitful outcome of this review, we surveyed modern trends in this arena of research and summarised the intricacies of new features to guide and prepare the sector for an Industry 5.0-ready healthcare system.

The significant increase in the demand for efficient electric energy storage during the past decade has promoted an increase in the production and use of Cd-containing batteries. On the one hand, the amount of toxic Cd-containing used batteries is growing, while on the other hand, Cd is on a list of critical raw materials (for Europe). Both of these factors call for the development of effective technology for Cd recovery from spent batteries. The present paper is aimed at providing a short review of the recent progress in Cd recovery from spent batteries. Statistical data from the past decade on the source of Cd, its global production, and Ni-Cd battery recycling are given in the introduction. A short overview of the pyro-and hydro-metallurgical methods of metal production is provided. Recent progress in Cd recovery by commercial methods during the past decade is reviewed.

Cenospheres are hollow particles in fly ash, a by-product of coal burning, and are widely used as a reinforcement when developing low-density composites called syntactic foams. This study has investigated the physical, chemical, and thermal properties of cenospheres obtained from three different sources, designated as CS1, CS2, and CS3, for the development of syntactic foams. Cenospheres with particle sizes ranging from 40 to 500 μm were studied. Different particle distribution by size was observed, and the most uniform distribution of CS particles was in the case of CS2: above 74% with dimensions from 100 to 150 μm. The CS bulk had a similar density for all samples and amounted to around 0.4 g·cm⁻³, with a particle shell material density of 2.1 g·cm⁻³. Post-heat-treatment samples showed the development of a SiO₂ phase in the cenospheres, which was not present in the as-received product. CS3 had the highest quantity of Si compared to the other two, showing the difference in source quality. Energy-dispersive X-ray spectrometry and a chemical analysis of the CS revealed that the main components of the studied CS were SiO₂ and Al₂O_3. In the case of CS1 and CS2, the sum of these components was on average from 93 to 95%. In the case of CS3, the sum of SiO₂ and Al₂O₃ did not exceed 86%, and Fe₂O₃ and K₂O were present in appreciable quantities in CS3. Cenospheres CS1 and CS2 did not sinter during heat treatment up to 1200 °C, while sample CS3 was already subjected to sintering at 1100 °C because of the presence of a quartz phase, Fe₂O₃ and K₂O. For the application of a metallic layer and subsequent consolidation via spark plasma sintering, CS2 can be deemed the most physically, thermally, and chemically suitable.

A low-density clay ceramic syntactic foam (CSF) composite material was successfully synthesized from illitic clay added by fly ash cenospheres (CS) using the semi-dry formation method. The content of CS varied in the range of 10, 30, 50 and 60 vol %. Furthermore, reference samples without cenospheres were produced for property comparison. The materials comprising different amount of the additives were fired at temperatures of 600, 950, 1000, 1050, 1100, 1150 and 1200 °C. Firing times were kept constant at 30 min. Processing characteristics of the materials were evaluated in terms of density achieved and shrinkage observed as functions of both the CS content and the sintering temperature. The compressive strength and water uptake were determined as application-oriented properties. Except for the reference and the low CS level samples, the materials show an increase in strength with the increase in firing temperature, and a decrease of mechanical reliability with a decrease in density, which is typical for porous materials. Exceptions are the samples with no or low (10 vol %) content of cenospheres. In this case, the maximum strength is obtained at an intermediate sintering temperature of 1100 °C. At a low density (1.10 and 1.25 g/cm³), the highest levels of strength are obtained after sintering at 1200 °C. For nominal porosity levels of 50 and 60 vol %, 41 and 26 MPa peak stresses, respectively, are recorded under compressive load.