Since many thermoelectrics are brittle in nature with low mechanical strength, improving their mechanical properties is important to fabricate devices such as thermoelectric power generators and coolers. In this work, multiwalled carbon nanotubes (CNTs) were incorporated into polycrystalline Bi_0.4Sb_1.6Te₃ through powder processing, which increased the flexural strength from 32 MPa to 90 MPa. Electrical and thermal conductivities were both reduced in the CNT containing materials, leading to unchanged figure of merit. Dynamic Young's and shear moduli of the composites were lower than the base material, while the Poisson's ratio was not affected by CNT doping.

Modulus–porosity relationships are critical for engineered bone tissue scaffold materials such as hydroxyapatite (HA), where porosity is essential to biological function. Resonant ultrasound spectroscopy (RUS) measurements revealed that the Young's modulus, E, and shear modulus, G, of both alumina and HA decrease monotonically with increasing volume fraction porosity, P, for 0.06 < P < 0.39 (alumina) and 0.05 < P < 0.51 (HA). Although the elastic moduli of porous materials have been measured by a number of different ultrasonic resonance techniques (of which the RUS technique is one example) and over the last decade the elastic moduli of many solids have been measured by the RUS technique, this study is the first systematic RUS study of porous materials. Comparison of E versus P data for alumina (which has been studied extensively) with literature data from several measurement techniques indicates the RUS technique is effective for modulus–porosity measurements. Another key result is that although the HA specimens included in this study have a unimodal pore size distribution, the details of the decrease in E and G with increasing P agree well with literature data for HA with both unimodal and bimodal pore size distributions. In addition, Poisson's ratio exhibits a local minimum in the porosity range of 0.2 < P < 0.25 for both HA and alumina, which may be related to the pore morphology evolution during sintering.