Surgical adhesives play a crucial role in tissue integration and repair, yet their application in wet conditions has been severely limited by inadequate adhesive strength and subpar biocompatibility. Furthermore, tissue adhesives have rarely been reported in cartilage tissue repair. In this study, a three-armed dopamine-modified hyaluronic acid derivative adhesive was prepared to function as a bio-inspired adhesive in moist environments. To meet the clinical requirements for cartilage tissue adhesion, we studied its chemical structure, including microscopic morphology, adhesion properties with materials and tissues, in vivo degradation rules, and biological evaluation. The OGMHA8-DOPA adhesive with the optimal aldehyde substitution degree and dopamine-grafting rate was determined by analyzing the experimental conditions. SEM results revealed that the cartilage tissue adhered to a porous interconnected structure. The excellent biocompatibility of the material not only facilitated chondrocyte adhesion but also supported their proliferation on its surface. Animal experiments have demonstrated that this material has no observable inflammatory response or incidence of fibrous capsule formation. The degradation timeline of the material extends beyond the duration of two weeks. The dopamine-modified adhesive exhibited a tight interfacial binding force between the biomaterial and cartilage tissue and excellent biocompatibility in watery tissue, revealing its potential for application in cartilage tissue repair and minimally invasive surgery.

Biodegradable materials are a next-generation invention for the treatment of congenital heart diseases. However, the corresponding technology used to develop ideal biomaterials still presents challenges. We previously reported the first biodegradable atrial septal defect (ASD) occluder made of poly-lactic acid (PLLA). Unfortunately, the PLLA occluder had a limited endothelialization effect. In this study, the surface of the occluder membrane was coated with sericin/CD34 antibodies to promote the growth of endothelial cells and the regeneration of defective tissue and enhance the repair of the atrial septal defect. The physicochemical properties of the coat on the surface of the fiber membrane were characterized. The sericin coat successfully covered the fiber surface of the membrane, and the thickness of the membrane increased with the sericin concentration. The swelling rate reached 230%. The microscopic observation of fluorescently labeled CD34 antibodies showed that the antibodies successfully attached to the fiber membrane; the fluorescence intensity of PLLA-SH5 was particularly high. The in vitro experiment showed that the PLLA-SH-CD34 fiber membrane was biocompatible and promoted the adhesion and proliferation of endothelial cells. According to our findings, the PLLA-SH-CD34 membrane provides a theoretical and technical basis for the research and development of novel biodegradable occluders.