Methylene blue (MB) is abundantly found in textile industrial effluent which can cause severe health problems for public and environmental ecology. Therefore, this study aimed to remove MB from textile wastewater using the activated carbon developed from Rumexabyssinicus. The adsorbent was activated using chemical and thermal methods, and then it was characterized by SEM, FTIR, BET, XRD, and pH zero-point charge (pHpzc). The adsorption isotherm and kinetics were also investigated. The experimental design was composed of four factors at three levels (pH (3, 6, and 9), initial MB concentration (100, 150, and 200 mg/L), adsorbent dosage (20, 40, and 60 mg/100 mL), and contact time (20, 40, and 60 min)). The adsorption interaction was evaluated using response surface methodology. The characterization of a Rumexabyssinicus activated carbon was found to have multiple functional groups (FTIR), an amorphous structure (XRD), crack with ups and down morphology (SEM), pHpzc of 5.03 and a high BET-specific surface area of 2522 m²/g. The optimization of MB dye removal was carried out using the Response Surface methodology coupled with the Box Behnken approach. The maximum removal efficiency of 99.9% was recorded at optimum conditions of pH 9, MB concentration of 100 mg/L, the adsorbent dosage of 60 mg/100 mL, and contact time of 60 min. Among the three adsorption isotherm models, the Freundlich isotherm model was the best fit with an experimental value at R² 0.99 showing the adsorption process was heterogeneous and multilayer whereas the kinetics study revealed that pseudo-second-order at R² 0.88. Finally, this adsorption process is quite promising to be used at an industrial level.

The potential for malachite green dye saturated effluent to severely affect the environment and human health has prompted the search for effective treatment technologies. Thus, this study was conducted with the goal of developing activated carbon from Rumex abyssinicus for the adsorptive removal of malachite green dye from an aqueous solution. Unit operations such as drying, size reduction, impregnation with H₃PO₄, and thermal activation were used during the preparation of the activated carbon. An experiment was designed considering four main variables at their respective three levels: initial dye concentration (50, 100, and 150 mg/L), pH (3, 6, and 9), contact period (20, 40, and 60 min), and adsorbent dosage (0.05, 0.01, and 0.15 g/100 mL). Optimization of the batch adsorption process was carried out using the Response Surface methodology's Box Behnken approach. The characterization of the activated carbon was described by SEM for surface morphology with cracks and highly porous morphology, FTIR for multi-functional groups O–H at 3506.74 cm⁻¹ and 3290.70 cm⁻¹, carbonyl group stretching from aldehyde and ketone (1900–1700 cm⁻¹), stretching motion of aromatic ring C=C (1543.12 cm⁻¹), stretching motion of –C–H (1500–1200 cm⁻¹), vibrational and stretching motion of –OH (1250.79 cm⁻¹), and vibrational motion of C–O–C (1049.32 cm⁻¹), pHpzc of 5.1, BET for the specific surface area of 962.3 m²/g, and XRD for the presence of amorphous structure. The maximum and minimum dye removal efficiencies of 99.9% and 62.4% were observed at their respective experimental conditions of (100 mg/L, 0.10 mg/100 mL, pH 6, and 40 min) and (100 mg/L, 0.15 mg/100 mL, pH 3, and 20 min), respectively. Langmuir, Freundlich, Toth, and Koble-Corrigan models were used to evaluate the experimental data, in which Koble-Corrigan model was found to be the best fit with the highest value of R² 0.998. In addition to this, the kinetic studies were undertaken using pseudo-first-order, pseudo-second-order, intraparticle diffusion, and Boyd models, and as a result, the pseudo-second-order model proved to have a better fit among the kinetic models. The kinetics and isotherm analysis revealed that the nature of the adsorption to be homogenous and monolayer surfaces driven by chemosorption. Furthermore, the thermodynamics study revealed the nature of adsorption to be feasible, spontaneous, and endothermic. On the other hand, the reusability study depicted the fact that the adsorbent can be utilized for five cycles with a negligible drop in the removal efficiencies from 99.9 to 95.2%. Finally, the low-cost, environmentally benign, and high adsorption capacity of the adsorbent material derived from Rumex abyssinicus stem could be used to treat industrial effluents.

The tannery industry inevitably generates toxic and catastrophic wastewater, which results in a huge threat to public health and water resources. Therefore, this work aimed to synthesize parthenium hysterophorus-based biochar–Fe₃O₄ composite for removal of Cr(VI) from tannery wastewater under 3⁴ full factorial experimental designs of the Box–Behnken, which was analyzed using response surface methodology under four independent factors of pH (3, 6, and 9), initial Cr(VI) concentrations (40, 70, and 100 mg/L), contact times (30, 60, and 90 min), and adsorbent doses (20, 60, and 100 mg/100 mL). This composite adsorbent was described by a high BET surface area of 237.4 m²/g, XRD prominent peaks, SEM morphology corroborate and FTIR multifunctionalities of O–H at 3296 cm⁻¹, the vibration of ketone C–OH at 1240 cm⁻¹, and the vibration of C–O–C at 1147 cm⁻¹ and Fe–O stretching at 542 cm⁻¹. The maximum Cr(IV) removal efficiency of 91.8% was recorded at an initial Cr(VI) concentration of 40 mg/L, pH of 3, adsorbent dose of 100 mg/100 mL, and a contact time of 90 min, whereas the minimum Cr(VI) removal of 17.3% was observed at an initial Cr(VI) concentration of 100 mg/L, 20 mg/100 mL of adsorbent dose, pH of 9, and contact time of 30 min. The concentration of Cr(VI) in real wastewater was determined to be 85.13 mg/L and its remediation was found to be 81.8%. Langmuir’s model was the best fit with experimental data at R² 0.99 and q_max 400 mg/g, showing that the adsorption process was homogenous and monolayer. In conclusion, the adsorption results were encouraging, and biochar–Fe₃O₄ appears to be a potential candidate for Cr removal from wastewater.

The environmental pollution and human health impacts associated with the discharge of massive dye-containing effluents necessitate a search for cost-effective treatment technology. Therefore, this research work is conducted with the objective of investigating the potential of Rumex abyssinicus-derived activated carbon (RAAC) for the adsorption of Brilliant Blue Reactive (BBR) dye from aqueous solutions. Chemical activation with H₃PO₄ followed by pyrolysis was used to prepare the adsorbent. Characterization of the developed adsorbent was done using proximate analysis, pH point of zero charge (pHpzc), scanning electron microscope (SEM), Fourier transform infrared spectrometer (FTIR), Brunauer, Emmett, and Teller (BET), and X-ray diffraction (XRD). The experimental design and the effect of independent variables including pH (2, 6, and 10), initial dye concentration (50, 100, and 150 mg/L), adsorbent dosage (0.05, 0.1, and 0.15 g/100 mL), and contact time (20, 50, and 80 min) were optimized using the response surface methodology (RSM) coupled with Box Behnken design (BBD). The analysis results revealed the exitance of high specific surface area of 524 m²/g, morphological cracks, and the presence of multiple functional groups like –OH, C=C, alkene, and amorphous structure. Maximum removal efficiency of 99.98% was attained at optimum working conditions of pH 2, contact time of 50 min, dye concentration of 100 mg/L, and adsorbent dosage of 0.15 mg/100 mL, reducing the pollutant concentration from 100 to 0.02 mg/L. Evaluation of the experimental data was done using Langmuir, Freundlich, Temkin, and Sips isotherm models, in which the Langmuir model was found to be the best fit with the experimental data at R² 0.986. This shows that the adsorbent surface is homogeneous and mono-layered. Furthermore, the kinetic study confirmed that the pseudo second-order model best describes the experimental data with R² = 0.999. In general, the research work showed that the low cost, environmental friendliness and high adsorption capabilities of the activated carbon derived from Rumex abyssinicus could be taken as an effective nt for the removal of BBR dye from aqueous solutions.