Titanium alloy, as a recognized difficult-to-cut material, places higher demands on the performance of cutting tools. Compared with the mainstream cemented carbide tools, PcBN tools have a higher life and better machining performance. In this paper, a new type of cubic boron nitride superhard tool was prepared by introducing Y₂O₃-stabilized ZrO₂ (YSZ) under high temperature and high pressure (1500 °C, 5.5 GPa), and the effect of the variation of YSZ addition on the mechanical properties of the tool was systematically analyzed, and the cutting performance of the tool was also analyzed by cutting TC4. It was found that a small amount of YSZ addition, which generated a sub-stable t-ZrO₂ phase during the sintering process, could improve the mechanical properties of the tool and increase its cutting life. When YSZ was added at 5 wt%, the flexural strength and fracture toughness of the composites reached the maximum values of 637.77 MPa and 7.18 MPa m^1/2, while the cutting life of the tools reached the maximum value of 2615.81 m. And when YSZ was added at 2.5 wt%, the hardness of the material reached the maximum value of 43.62 GPa.

Ceramic corundum abrasives were prepared using pseudo-boehmite as a raw material via the sol-gel method. Additives can significantly change the microscopic morphology of abrasives and improve mechanical properties. When 2 wt% CaO-TiO₂-SiO₂ with a molar ratio of 3:4:9 was added, samples with the best morphology and mechanical properties were obtained. Single-particle compressive strength, density, Vickers hardness, and average grain size were 51.45 N, 3.94 g·cm⁻³, 16.43 GPa, and 0.98 μm, respectively. We compared the same additive system with abrasives prepared by ball milling, and found that ball milling was beneficial for obtaining denser and smaller grain size abrasives. On the other hand, abrasives obtained without ball milling had relatively higher single-particle compressive strength. Additionally, the additives are non-precious metal oxides, which can reduce the cost of the synthesis process. In addition, there has been discussion of the connection between microstructure and mechanical characteristics.