Spinel ferrites are versatile, low-cost, and abundant metal oxides with remarkable electronic and magnetic properties, which find several applications. Among them, they have been considered part of the next generation of electrochemical energy storage materials due to their variable oxidation states, low environmental toxicity, and possible synthesis through simple green chemical processing. However, most traditional procedures lead to the formation of poorly controlled materials (in terms of size, shape, composition, and/or crystalline structure). Thus, we report herein a cellulose nanofibers-mediated green procedure to prepare controlled highly porous nanocorals comprised of spinel Zn-ferrites. Then, they presented remarkable applications as electrodes in supercapacitors, which were thoroughly and critically discussed. The spinel Zn-ferrites nanocorals supercapacitor showed a much higher maximum specific capacitance (2031.81 F g⁻¹ at a current density of 1 A g⁻¹) than Fe₂O₃ and ZnO counterparts prepared by a similar approach (189.74 and 24.39 F g⁻¹ at a current density of 1 A g⁻¹). Its cyclic stability was also scrutinized via galvanostatic charging/discharging and electrochemical impedance spectroscopy, indicating excellent long-term stability. In addition, we manufactured an asymmetric supercapacitor device, which offered a high energy density value of 18.1 Wh kg⁻¹ at a power density of 2609.2 W kg⁻¹ (at 1 A g⁻¹ in 2.0 mol L⁻¹ KOH electrolyte). Based on our findings, we believe that higher performances observed for spinel Zn-ferrites nanocorals could be explained by their unique crystal structure and electronic configuration based on crystal field stabilization energy, which provides an electrostatic repulsion between the d electrons and the p orbitals of the surrounding oxygen anions, creating a level of energy that determines their final supercapacitance then evidenced, which is a very interesting property that could be explored for the production of clean energy storage devices.

Ceria-based nanostructures, employed as catalytic supports for noble and non-noble metals, are well-known for their remarkable activity in steam-reforming reactions, exceptional resistance to degradation, and thermal stability. However, the catalytic activity and selectivity of such systems are strongly dependent on the size and shape of ceria, making it possible to tune the oxide properties, affecting catalyst design and performance. The rational manipulation of ceria nanostructures offers various features that directly impact steam-reforming transformations, including the possibility of tuning oxygen vacancies, redox properties, and oxygen storage capacity. Thus, the importance of shape control in ceria nanomaterials is highlighted herein, emphasizing how the surface atomic configurations (exposure of different facets) significantly impact their efficiency. Although the main focus of this review is to discuss how the catalyst design may affect the performance of hydrogen production, some other elemental studies are shown, when necessary, to exemplify the level of deepness (or not) that literature has reached. Thus, an overview of ceria properties and how the physicochemical control of nanostructures contributes to their tuning will be presented, as well as a discussion regarding elemental materials design and the most prominent synthetic procedures; then, we select some metals (Ni, Co, and Pt) to discuss the understanding of such aspects for the field. Finally, challenges and perspectives for nanoengineering catalysts based on shape-controlled ceria nanostructures will be described to possibly improve the performance of designed catalysts for steam-reforming reactions. Although there are other literature reviews on ceria-based catalysts for these reactions, they do not specifically focus on the influence of the size and shape of the oxide.