Human bones are biological examples of functionally graded lattice capable to withstand large in vivo loading and allowing optimal stress distribution. Disruption of bone integrity may require biocompatible implants capable to restore the original bone structure and properties. This study aimed at comparing mechanical properties and biological behavior in vitro of uniform (POR‐FIX) and graded (POR‐VAR) Cobalt‐chrome alloy lattice structures manufactured via Selective Laser Melting. In compression, the POR‐VAR equivalent maximum stress was about 2.5 times lower than that of the POR‐FIX. According to the DIC analysis, the graded lattice structures showed a stratified deformation associated to unit cells variation. At each timepoint, osteoblast cells were observed to colonize the surface and the first layer of both scaffolds. Cell activity was always significantly higher in the POR‐VAR (p < 0.0005). In terms of gene expression, theOPG/RANKLratio increased significantly over time (p < 0.0005) whereasIL1βandCOX2significantly decreased (7 day vs 1 day;p < 0.0005) in both scaffolds. Both uniform‐ and graded‐porosity scaffolds provided a suitable environment for osteoblasts colonization and proliferation, but graded structures seem to represent a better solution to improve stress distribution between implant and bone of orthopedic implants.

Stainless steel (SS) alloys produced by laser-based powder bed fusion (LPBF) offers comparable and sometime superior mechanical properties compared to conventionally processed materials. Some of these steels have been extensively studied over the last decade; however additively manufactured martensitic SS, such as AISI 420, need further research in characterizing their post-built quality and mechanical behaviour. This lack of information on martensitic SS is not consistent with their growing demand in the automotive, medical and aerospace industries due to their good corrosion resistance, high hardness and good tensile properties. Selection of the appropriate process parameters and post treatments plays a fundamental role in determining final properties. For this reason, the effect of LPBF process parameters and different heat treatments on density, defect characteristics and locations, roughness and mechanical properties of AISI 420 were investigated in this paper. A first experimental campaign was carried out to establish a set of suitable process parameters for industrial applications. Starting from this result, detected defect properties were investigated by computed tomography (CT) scans. Dimensions, sphericity and distributions of defects inside the volume were analysed and compared between samples manufactured with different parameters. In the second part of the paper, the influence of process and post-process conditions on mechanical properties was investigated. The final presented results establish a correlation between the employed production cycle and the resulting properties of LPBF AISI 420 specimens.

Studies have shown the influence of WAAM process parameters on mechanical properties, bead formation, dimensional accuracy, and microstructure. However, metal transfer modes and their interactions with input variables have not been investigated thoroughly. Therefore, short/spray, pulse and double pulse modes were investigated in this study at different current levels. Bead-on-plate trials were conducted by depositing ER70S-6 wire to investigate bead morphology, dilution, microstructure, and hardness. The study was supported by a detailed statistical approach, including analysis of variance (ANOVA) and regression analysis. Similarly, the combined effects of hatch distance and current were studied on bead formation in multi-layer deposits. Moreover, a thin wall and a cubic structure were deposited to realize the WAAM capability for larger depositions. The microstructures of thin wall and cubic structure were analyzed using optical microscopy (OM) and scanning electron microscopy (SEM). The study concludes that metal transfer modes at various currents significantly influence bead geometry, microstructure and hardness. The microstructure of bead-on-plate trials show fine lamellar structure at low current in all modes. Higher current results in coarse grains with a polygonal and columnar morphology. The hardness shows a decreasing trend as the current increases. The combined effects of current and hatch distance alter bead morphology; however, an optimized combination yields smoother surfaces. The microstructure of thin wall showed a slight anisotropy along the building direction. The presence of small pores was witnessed from OM and SEM images. Similarly, the cubic structure showed a more homogeneous microstructure with much lower porosity. The hardness profile of the thin wall exhibited small fluctuations along the building direction, while that of the cubic structure was more uniform.