TiO₂ sol was produced by the sol-gel method through the hydrolysis and the aging of tetrabutyl titanate and the TiO₂ film was obtained by dipping and uniform lifting of the acid-treated and ultrasound-treated clean glass slides into the TiO₂ sol followed by aging, drying, and calcination. The effect of the hydrolysis control agents to the formed sol was researched and the crystalline state, the morphology, and the photocatalytic properties of the products after calcination were characterized. The structural morphology, the contact angles before and after illumination, and the self-cleaning properties of the TiO₂ film were characterized as well. The results showed that by using acetylacetone as the hydrolysis control agent, the formed TiO₂ sol had relatively high stability. The product after the calcination of the TiO₂ sol was of single anatase type with crystalline size of 18–20 nm and it could degrade nearly 100% of methylene blue after 90 min illumination. The formed TiO₂ film is compact, continuous, smooth, and had the properties of super-hydrophilicity (after 30 min illumination due to its contact angle decreasing from 21° to nearly 0°) and anti-fogging capability, which indicated its excellent self-cleaning property.

In order to reduce the primary particle size of zinc oxide (ZnO) and eliminate the agglomeration phenomenon to form a monodisperse state, Zn²⁺ was loaded on the surface of amorphous silica (SiO₂) by the hydrogen bond association between hydroxyl groups in the hydrothermal process. After calcining the precursors, dehydration condensation among hydroxyl groups occurred and ZnO nanoparticles supported on amorphous SiO₂ (ZnO–SiO₂) were prepared. Furthermore, the SEM and TEM observations showed that ZnO nanoparticles with a particle size of 3–8 nm were uniformly and dispersedly loaded on the surface of amorphous SiO₂. Compared with pure ZnO, ZnO–SiO₂ showed a much better antibacterial performance in the minimum inhibitory concentration (MIC) test and the antibacterial properties of the paint adding ZnO–SiO₂ composite.