Metallurgical grade alumina is produced worldwide through the well-known Bayer process, which unavoidably generates bauxite residue (BR, also known as red mud) in almost equal amounts to alumina. This study aims the valorization of BR through a smelting-reduction process to obtain calcium aluminate slags that can be a proper feed for alumina recovery via the Pedersen process. It investigates the thermodynamics and characteristics of the slags and pig iron produced from mixtures of BR, a bauxite beneficiation byproduct, and lime. In this context, the evolution of the different phases in the slags is studied with advanced analytical techniques and thermodynamic calculations. According to the results, a CaO/Al₂O₃ mass ratio within 1.3 to 1.4 in the slags can yield more Al₂O₃-containing leachable phases, such as CaO·Al₂O₃ and 12CaO·7Al₂O₃. The cooling dictates the amount and the characteristics of these phases, and the slower cooling rate yields improved slag characteristics. The distribution of the elements between the slag and metal phases shows that iron is separated, and the majority of the P, Cr, Ni, and V are distributed in the produced pig iron, while S, Ti, and Si are mostly concentrated in the slags.

Fe-26.38Si-9.35B eutectic alloy is proposed as a phase change material (PCM) as it exhibits high latent heat, high thermal conductivity, moderate melting point, and low cost. For successful implementation of it in the latent heat thermal energy storage (LHTES) systems, we investigate the use of graphite as a refractory material that withstands long-term melting/solidification in contact with the Fe-26.38Si-9.35B alloy. The PCM has been thermally cycled up to 1–4 times below and above its melting point at the temperature interval of 20 °C or 100 °C. It is observed that this eutectic alloy shows good thermal stability over a small temperature range of 1057–1257 °C. Some SiC and B₄C solid precipitation will be formed at the top of the alloy. However, it does not seem to increase with time. The graphite crucible as a refractory material will produce a protective layer of SiC and B₄C that will hinder the interaction between the PCM and the crucible. The small volume change during solidification will not break the graphite crucible during cycling. The chemical wear or dissolution of the crucible is negligible. It demonstrates the viability of Fe-26.38Si-9.35B alloy as a heat storage material in this type of container.

A high temperature process for recycling spent nickel-metal hydride rechargeable batteries has been recently developed at SINTEF/NTNU. The spent battery modules were first frozen with liquid nitrogen for the de-activation and brittle fracture treatment. The broken steel scraps and plastics were then separated by the mechanical classification and magnetic separation. The remaining positive and negative electrodes, together with the polymer separator, were heated to 600-800oC in order to remove the organic components and further separate the Ni-based negative electrode. XRF analyses indicate that the heat-treated materials consist mainly of nickel, rare earth and cobalt oxides. The valuable rare earth oxides were further recovered by the high-temperature slagging treatment. The waste metallurgical slags, consist mainly of SiO2 and CaO, were used as the rare earth oxide absorbent. After the high temperature slagging treatment, over 98% of nickel and cobalt oxides were reduced to the metal phase; meanwhile almost all rare earth oxides remain in the molten slags. Furthermore, EPMA and XRF analyses of the slag samples indicate that the rare earth oxides selectively precipitate in the forms of solid xSiO2?yCaO?zRe2O3. The matrix of slag phase is Re2O3 deficient, typically being less than 5 wt%. This provides a sound basis to further develop the high-temperature process of concentrating the Re2O3 oxides in slags.