Poly(ethylene terephthalate) (PET) fibers (virgin, waste, and mixed) were incorporated in the composite poly(methyl methacrylate) (PMMA)–wood. Hybrid composite panels were prepared by pressure molding. Toluene-2,4-diisocyanate (TDI) and (3-mercaptopropyl)trimethoxysilane (MPTMS) were used as cross-linking bonding agents for modification of wood fibers. Influence of cross-linking bonding agents, structure, and composition of PET fibers was examined by studying thermomechanical properties as well as moisture absorption. Moisture absorption was lower for composites with bonding agents. Mechanical testing revealed that the addition of PET fibers drastically enhances properties of the composites. Covalent and hydrogen bonds formed with the addition of bonding agents have also improved mechanical properties compared to the untreated composites.

Polymer-bonded magnets are a class of composite material that combines the magnetic properties of metal particles and the molding possibility of a polymeric matrix. This class of materials has shown huge potential for various applications in industry and engineering. Traditional research in this field has so far mainly focused on mechanical, electrical or magnetic properties of the composite, or on particle size and distribution. This examination of synthesized Nd-Fe-B-epoxy composite materials includes the mutual comparison of impact toughness, fatigue, and the structural, thermal, dynamic-mechanical, and magnetic behavior of materials with different content of magnetic Nd-Fe-B particles, in a wide range from 5 to 95 wt.%. This paper tests the influence of the Nd-Fe-B content on impacting the toughness of the composite material, as this relationship has not been tested before. The results show that impact toughness decreases, while magnetic properties increase, along with increasing content of Nd-Fe-B. Based on the observed trends, selected samples have been analyzed in terms of crack growth rate behavior. Analysis of the fracture surface morphology reveals the formation of a stable and homogeneous composite material. The synthesis route, the applied methods of characterization and analysis, and the comparison of the obtained results can provide a composite material with optimum properties for a specific purpose.

Background/Objectives: Efficient wound treatment embraces the management of four overlapping phases, starting with hemostasis, an immediate physiological response aimed at stopping bleeding from damaged blood vessels caused by skin injury. This paper proposes an innovative, nature-based hemostatic biomaterial designed to assist natural self-healing regenerative mechanisms. Methods: Light, transparent, and skin-adhesive films based on κ-carrageenan, meadow polyfloral honey, and Calendula officinalis flower extract were fabricated via solution casting. Comprehensive characterization revealed the physicochemical, structural, swelling, and barrier properties and the influence of each bioactive compound utilized for film preparation. Results: The samples subcutaneously implanted in Wistar rats induced vascularization, deposition of collagen, and orientation of collagen fibers while being fully phagocytosed and gradually biodegraded. The rat tail-cut model demonstrated that the films significantly reduced blood loss (0.1875 ± 0.0732 g) compared to the control (0.7837 ± 0.3319 g), and hemostasis was achieved notably faster (355.75 ± 71.42 s) than in the control group (704.25 ± 85.29 s). The rat liver punch biopsy model confirmed reduced blood loss (2.8025 ± 1.5174 g) and shorter time to hemostasis (303.25 ± 77.90 s) compared to the control (3.1475 ± 1.5413 g, 383.00 ± 36.53 s). Conclusions: The results indicate the great potential of the fabricated films as hemostatic wound dressings.

Wood–plastic composites (WPCs) are some of the most common modern composite materials for interior and exterior design that combine natural waste wood properties and the molding possibility of a thermoplastic polymer binder. The addition of reinforcing elements, binding agents, pigments, and coatings, as well as changes to the microstructure and composition, can all affect the quality of WPCs for particular purposes. To improve the properties, hybrid composite panels of WPCs with 30 wt. % and 40 wt. % of wood content and reinforced with one or three metal grid layers were prepared sequentially by extrusion and hot pressure molding. The results show an average 20% higher moisture absorption for composites with higher wood content. A high impact test (HIT) revealed that the absorbed energy of deformation increased with the number of metal grid layers, regardless of the wood content, around two times for all samples before water immersion and around ten times after water absorption. Also, absorbed energy increases with raised wood content, which is most pronounced in three-metal-grid samples, from 21 J to 26 J (before swelling) and from 15 J to 24 J (after swelling). Flexural tests follow the trends observed by HIT, indicating around 65% higher strength for samples with three metal grid layers vs. samples without a metal grid before water immersion and around 80% higher strength for samples with three metal grid layers vs. samples without a grid after water absorption. The synthesis route, double reinforcing (wood and metal), applied methods of characterization, and optimization according to the obtained results provide a WPC with improved mechanical properties ready for an outdoor purpose.

Wood plastic composites (WPC) are currently one of the most popular building materials, especially for areas exposed to moisture, UV radiation or large temperature differences. In the first stage, the mechanically shredded wood was mixed with the matrix of waste polyethylene (WPE) and processed into briquettes using the extrusion process. In the second stage, the briquettes are hybridized with five layers of metal mesh and pressed at an elevated temperature to produce WPC with improved mechanical properties. SEM is used for the microstructural analysis of WPC. The chemical analysis is carried out using FTIR. The results of the impact strength and bending measurements show a strong improvement in the mechanical properties of the WPC hybridized with metal mesh layers. All WPC samples show a high resistance to moisture, which is confirmed by the results of the mechanical measurements after exposure to water. In terms of sustainable development and environmental protection, the materials used for WPC production are waste and/or recycled, indicating a longer life cycle of WPC that could be analyzed in depth in future research.