A facile strategy for the design of porous supports was obtained by modifying the sol-gel method followed by the wet impregnation technique. In this respect, herein, the acidity of the γ-Al₂O₃ phase was modulated by adding basic MgO, La₂O₃ or ZnO promoters to form binary supported catalysts. The Ni and Co dispersion on the supports associated with their tunable acidity and morphologies resulted in highly porous supported alumina-based catalysts. The physicochemical properties of the solids were comprehensively investigated by XRD, textural properties, Raman and FTIR spectroscopy, SEM-EDS, TEM, EPR and XPS analyses. The catalytic performances in the esterification of glycerol in the presence of acetic acid (EG) for the acetins production were evaluated. The highly dispersed NiO and Co₃O₄ active species on binary porous supports produced synergistic effects appearing to be the reason for the activity of the solids in the EG reaction. Under the optimized reaction conditions, NiCo/MgO-Al₂O₃ was found to be a robust solid with superior catalytic performance and improved stability in four reaction cycles with 65.0% of glycerol conversion with an exclusive selectivity of 53% for triacetin. The presence of Co²⁺/Co³⁺ and Ni²⁺ strongly interacting with the spinel γ-Al₂O₃ and MgAl₂O₄ phases, the latter having a large number of lattice oxygen species, was considered another active component besides those of Ni and Co in the esterification of glycerol.

A series of the Cr-containing erbium substituted yttrium iron garnet ferrites (ECYIG) was synthesized with distinct Cr amounts, herein referred to as Y₃(Er_0.02Fe₅Cr_1−x)O₁₂, where x refers to Cr amounts from 0 to 0.05. The catalytic performance of the solids was investigated in ethylbenzene oxidation in the presence of hydrogen peroxide to assess the role of Cr and Er present in the YIG garnet lattice for fine chemistry compound production. Raman spectroscopy, HRTEM, EPR and FTIR revealed that the insertion of Er (at a fixed amount of 2%) in dodecahedral sites had a great impact on the catalytic activity of the garnets. Both Er³⁺ and Y³⁺ in the lattice simultaneously provided structural stability to the garnet structure in any harsh environment. XPS and EPR indicated that the Cr³⁺ ions replaced those of Fe³⁺ located in both octahedral and tetrahedral sites of the YIG garnets. The Cr³⁺ ions acted as electronic promoter to increase the oxidation rate of the Fe³⁺ active species responsible for activating the EB molecule. SEM-EDS demonstrated that the solids having Cr amounts lower than 4% experienced the most severe deactivation due to the Cr leaching and strong carbon species adsorption on the surface of the catalysts, which decreased their efficiency in the reaction.