This study describes the preparation and evaluation of phenol–furfural resin (PFR) from bagasse and its nanocomposites for electrically conductive adhesive (ECA) application. PFR was prepared with furfural extracted from bagasse using a modified acid digestion method. Three different formulations of PFR nanocomposites with conductive nanoparticles, i.e., PFR-silver, PFR-graphite, and PFR-silver + graphite, were prepared using 20, 40, and 60 w/w% of fillers via the impregnation method. The resultant products were characterized using FT-IR, SEM, EDS, and XRD spectroscopy. Electrical conductivity was measured using a four-probe technique, while band gap was calculated via Tauc plots. The results exhibited a significant rise in electrical conductivity of insulating virgin PFR from 2.6 × 10⁻⁴ Scm⁻¹ to 8.2 × 10⁻¹ Scm⁻¹ with a 40 and 20 w/w% blend of Ag and graphite in PFR. This synergism was exhibited because graphite and Ag NPs supply excellent junctions for building networks. Both tend to coalesce due to van der Waals forces and high surface energies. Therefore, conductive pathway numbers can be increased, and the contact area can be effectively enlarged. This ternary composite exhibited the lowest bandgap energy value, i.e., 3.1 eV. Thermogravimetric temperature values T₀ and T_deg were increased up to 120 °C and 484 °C, respectively, showing a significant increase in thermal stability. Therefore, the resultant nanocomposite material has good potential to be employed as an ECA in the electronic industry.

This study endeavors the preparation and evaluation of Phenol Furfural Resin (PFR) from bagasse and its nanocomposites for Electrically Conductive Adhesives (ECAs) application. PFR was prepared with the furfural extracted from bagasse using modified acid digestion method. Three different formulations of PFR nanocomposites with conductive nanoparticles i.e., PFR-silver, PFR-graphite, and PFR-silver + graphite were prepared using 20-60 w/w% of fillers via impregnation method. Resultant products were characterized by FT-IR, SEM, EDS and XRD spectroscopy. Electrical conductivity was measured using four probe technique while band gap was calculated via Tauc plot. Virgin PFR has shown poor conductivity up to 2.6 × 10^-4 Scm^-1 while the highest conductivity achieved was 8.2 × 10^-1 Scm^-1 for nanocomposite constituted silver, graphite, and PFR with 40:30:20 ratios respectively. This synergism was exhibited because graphite and Ag NPs supply excellent junctions for building networks. Both tend to coalesce due to van der Waals forces and high surface energies, therefore conductive pathways numbers can be increased, and contact area can be effectively enlarged. This ternary composite has exhibited the lowest bandgap energy value i.e., 3.1 eV. Thermogravimetric temperatures T₀ and T_deg values were increased up to 120 °C and 484 °C respectively, showing significant increase in thermal stability. Therefore, the resultant nanocomposite material has good potential to be employed as ECAs in electronic industry.

This study endeavors the preparation and evaluation of Phenol Furfural Resin (PFR) from bagasse and its nanocomposites for Electrically Conductive Adhesives (ECAs) application. PFR was prepared with the furfural extracted from bagasse using modified acid digestion method. Three different formulations of PFR nanocomposites with conductive nanoparticles i.e., PFR-silver, PFR-graphite, and PFR-silver + graphite were prepared using 20-60 w/w% of fillers via impregnation method. Resultant products were characterized by FT-IR, SEM, EDS and XRD spectroscopy. Electrical conductivity was measured using four probe technique while band gap was calculated via Tauc plot. Virgin PFR has shown poor conductivity up to 2.6 × 10-4 Scm-1 while the highest conductivity achieved was 8.2 × 10-1 Scm-1 for nanocomposite constituted silver, graphite, and PFR with 40:30:20 ratios respectively. This synergism was exhibited because graphite and Ag NPs supply excellent junctions for building networks. Both tend to coalesce due to van der Waals forces and high surface energies, therefore conductive pathways numbers can be increased, and contact area can be effectively enlarged. This ternary composite has exhibited the lowest bandgap energy value i.e., 3.1 eV. Thermogravimetric temperatures T0 and Tdeg values were increased up to 120 °C and 484 °C respectively, showing significant increase in thermal stability. Therefore, the resultant nanocomposite material has good potential to be employed as ECAs in electronic industry.

The rapid development in industries manufacturing plastic bags is taking serious consideration to save the environment and human health, one way or the other. This study examines the composition of degradable and non-degradable plastic bags collected from the markets of different sectors of Islamabad. Hundred samples of both Degradable and non-degradable plastic bags were collected from the open market. The concentrations, proportion, and patterns of different heavy metals (additives) were used in the production of both degradable and non-degradable plastic bags by using the standard method with the help of Hands Held X-Ray Fluorescent (HHXRF) instrument. Samples results of the study showed Titanium, Calcium and Copper used in massive amounts, some of the toxic metals i.e., Arsenic, Lead, Cadmium, Chromium and Mercury were also detected. This study also reveals that degradable plastic bags might be more hazardous than non-degradable plastic bags because due to the Photolytic properties of additives used in degradable plastic bags when the chains of polymers break, the heavy metals are released in environment and become the part of it. So, concern department like Ministry of climate change and Pakistan Environmental Protection Agency should take serious step to control these serious issues.