Cemented polished tapered femoral stems (PTS) made of cobalt–chrome alloy (CoCr) are a known risk factor for periprosthetic fracture (PPF). The mechanical differences between CoCr-PTS and stainless-steel (SUS) PTS were investigated. CoCr stems having the same shape and surface roughness as the SUS Exeter^® stem were manufactured and dynamic loading tests were performed on three each. Stem subsidence and the compressive force at the bone–cement interface were recorded. Tantalum balls were injected into the cement, and their movement was tracked to indicate cement movement. Stem motions in the cement were greater for the CoCr stems than for the SUS stems. In addition, although we found a significant positive correlation between stem subsidence and compressive force in all stems, CoCr stems generated a compressive force over three times higher than SUS stems at the bone–cement interface with the same stem subsidence (p < 0.01). The final stem subsidence amount and final force were greater in the CoCr group (p < 0.01), and the ratio of tantalum ball vertical distance to stem subsidence was significantly smaller for CoCr than for SUS (p < 0.01). CoCr stems appear to move more easily in cement than SUS stems, which might contribute to the increased occurrence of PPF with the use of CoCr-PTS.

It is well known that cracks are observed on the surface without load when pure nickel is left in ambient air after hydrogen charge. It has been due to the decomposition of nickel hydride generated during hydrogen charging. In the present work, microcracks were investigated at the surface and inside the specimen with suppressing the decomposition of nickel hydride in polycrystalline pure nickel. As a result, microcracks initiate in the nickel matrix near the hydride inside the specimen before hydride decomposition. The microcracks grow toward the specimen’s surface as hydride decomposition.